目的 提高医用PVC表面的抗菌性能。方法 采用sol-gel法制备ZnO溶胶，以P25（商品TiO2）悬浮液为掺杂组分，制备了不同TiO2质量分数（20%、40%、60%、80%）的TiO2-ZnO复合悬浮液，通过提拉法将ZnO、TiO2-ZnO、TiO2悬浮液均匀地涂覆在医用PVC材料表面。采用XRD、SEM等技术考察了复合膜的结构和性能。采用平板菌落计数法测定了不同膜材料对大肠杆菌的光催化杀菌性能和抗细菌粘附性能。结果 当TiO2质量分数为20%时，TiO2-ZnO薄膜的光催化活性高于ZnO；当TiO2质量分数为40%、60%、80%时，样品的光催化活性相差不大且都低于ZnO。对ZnO膜和TiO2-ZnO复合膜的细菌抗粘附性和光催化杀菌性的测试结果表明，ZnO膜和不同TiO2质量分数的TiO2-ZnO复合膜都具有一定的抗粘附性和光催化灭菌性。在抗粘附方面，TiO2质量分数为20%的TiO2-ZnO复合膜的性能最好，对大肠杆菌的粘附率仅为2.6%，优于ZnO膜和TiO2膜。在光催化灭菌性方面，在波长为365 nm的紫外光照下，样品对大肠杆菌杀灭能力高低顺序为TiO2≈20%TiO2-ZnO>80% TiO2-ZnO>ZnO。结论 涂覆ZnO溶胶和TiO2悬浮液混合溶胶可以明显提高医用PVC表面的抗细菌粘附性能和光催化灭菌活性，而且当TiO2质量分数为20%时，TiO2-ZnO具备最好的抗菌性能。

The work aims to improve antibacterial properties of medical grade PVC surface. ZnO sol was prepared in sol-gel method, TiO2-ZnO composite suspension of different TiO2 mass fraction (20%, 40%, 60% and 80%) was prepared with P25 (commodity TiO2) suspension as doping constituent. ZnO, TiO2-ZnO and TiO2 suspensions were coated on medical-grade PVC materials uniformly in pulling method. Structure and properties of the composite film were characterized by virtue of XRD and SEM techniques. The photocatalytic antimicrobial activity and bacterial adhesion resistance of different coating materials to Escherichia coli were determined in the method of plate culture count. Photocatalytic activity of theTiO2-ZnO film doped with 20 wt% TiO2 was better than that of ZnO; photocatalytic activity of the samples doped with 40 wt%, 60 wt% and 80 wt% TiO2 was close and lower than that of the pure ZnO. ZnO as well as TiO2-ZnO composite films doped with different mass fractions of TiO2 exhibited certain bacterial adhesion resistance and antimicrobial activity. Among these samples, the sample doped with 20 wt% TiO2 exhibited best bacterial adhesion resistance. The adherent mass fraction of Escherichia coli was only 2.6%, superior to that of ZnO and TiO2 films. Under UV irradiation with wave length of 365 nm, rank of antimicrobial activity among the samples was TiO2≈20 wt% TiO2 >80 wt% TiO2>ZnO. The bacterial adhesion resistance and photocatalytic antimicrobial activity of medical-grade PVC materials can be enhanced by dip coating with ZnO sol and TiO2 suspension. Besides, TiO2-ZnO doped with 20 wt% TiO2 has the best antimicrobial activity.