WANG Cheng-lei,LIANG Chao-jie,ZHOU Cheng-hua,ZHANG Ke-xiang,XIE Ying-guang,LIN De-min.High Temperature Friction and Wear Properties of Laser Cladding Ni60 Coating Modified with Rare Earth on 6063 Aluminum Alloy Base[J],49(10):69-80 |
High Temperature Friction and Wear Properties of Laser Cladding Ni60 Coating Modified with Rare Earth on 6063 Aluminum Alloy Base |
Received:August 05, 2020 Revised:October 20, 2020 |
View Full Text View/Add Comment Download reader |
DOI:10.16490/j.cnki.issn.1001-3660.2020.10.008 |
KeyWord:laser cladding aluminum alloy rare earth regulation friction and wear at high temperature Ni60 |
Author | Institution |
WANG Cheng-lei |
1.School of Materials Science and Engineering, Guilin University of Electronic Technology, Guilin , China |
LIANG Chao-jie |
1.School of Materials Science and Engineering, Guilin University of Electronic Technology, Guilin , China |
ZHOU Cheng-hua |
2.Hunan Industry Polytechnic, Changsha , China |
ZHANG Ke-xiang |
1.School of Materials Science and Engineering, Guilin University of Electronic Technology, Guilin , China |
XIE Ying-guang |
1.School of Materials Science and Engineering, Guilin University of Electronic Technology, Guilin , China |
LIN De-min |
3.Guangxi Mingxin Chassis Parts Co., Ltd, Guilin , China |
|
Hits: |
Download times: |
Abstract: |
In order to improve the comprehensive performance of aluminum alloy, the surface of 6063 aluminum alloy was modified with Ni60, Ni60+4%CeO2, Ni60+5%Y2O3 and Ni60+5%La2O3 by using laser cladding technology. Hardness experiments, high temperature friction and wear behaviors were carried out. The wear resistance and wear mechanism of each sample and the influence of rare earth on the wear resistance and wear mechanism of the cladding layer by analyzing the friction coefficient, wear tracks, wear amount, phase, composition and micro-morphology after wear of the sample. The hardness of the cladding layer added with rare earth increase significantly and the hardness of the cladding layer presented a gradient distribution. With the increase of load and wear temperature, the wear mechanism of 6063 Al changed from mild to severe wear, the order was two-body abrasive wear to adhesive wear, and then, to severe melting wear and oxidative wear. The wear mechanism of Ni60 cladding layer was mainly peeling wear, oxidation wear and slight ploughing wear. With the increase of load and wear temperature, the degree of peeling wear became more and more serious. With the increase of load and wear temperature of the cladding layer with the optimal rare earth content, the wear mechanism gradually changed from ploughing wear to delamination wear, and contained oxidation wear and plough wear. Compared with the Ni60 cladding layer, the high-temperature friction and wear properties of the cladding layer with the best rare earth content were significantly improved. Compared with the three kinds of rare earth cladding layers, the order of high temperature friction and wear performance from good to poor is Ni60+4%CeO2 cladding layer, Ni60+5%Y2O3 cladding layer, Ni60+5%La2O3 cladding layer. |