| PEI Di,DENG Peng-yuan,LIU Zhi-jun,WANG Li.Preparation and Property Evaluation of NbC Coating Deposited on 316L Stainless Steel[J],48(3):105-111 |
| Preparation and Property Evaluation of NbC Coating Deposited on 316L Stainless Steel |
| Received:August 03, 2018 Revised:March 20, 2019 |
| View Full Text View/Add Comment Download reader |
| DOI：10.16490/j.cnki.issn.1001-3660.2019.03.015 |
| KeyWord:NbC coating 316L SS mechanical properties corrosion resistance hemocompatibility |
| Author | Institution |
| PEI Di |
1.a.School of Petrochemical Engineering, Yinchuan Energy University, Yinchuan , China |
| DENG Peng-yuan |
2.No.703 Research Institute of CSIC, Harbin , China |
| LIU Zhi-jun |
1.b.School of Mechanics and Automotive Engineering, Yinchuan Energy University, Yinchuan , China |
| WANG Li |
1.a.School of Petrochemical Engineering, Yinchuan Energy University, Yinchuan , China |
|
| Hits: |
| Download times: |
| Abstract: |
| The work aims to investigate the corrosion resistance and blood compatibility of NbC as biological inert coatings in simulated body fluids, so as to provide a reference for improving the performance of 316L stainless steel as a cardiac stent. NbC coating was prepared by the physical vapor deposition (PVD) widely used in surface modification area and the coating properties were improved by optimized process to obtain high adhesion force and density. Scanning electron microscope (SEM), Atomic force microscope (AFM), X-Ray diffraction (XRD), Nano-indentation and Scratch test were used to investigate the microstructure and mechanical properties. The potentiodynamic polarization curve and platelet adhesion test were used to characterize the corrosion resistance and evaluate hemocompatibility of NbC coatings. With the increasing of substrate temperature, the mechanical properties, corrosion resistance and blood compatibility of NbC coatings were significantly improved, and the hardness and elastic modulus of NbC coatings increased from (12.5±0.2) GPa and (213±0.8) GPa to (24.5±0.4) GPa and (275±1.1) GPa, respectively. The self-corrosion rate was significantly optimized from 8.76?10?6 A/cm2 to 1.98?10?8 A/cm2. In general, the NbC coating has the same stability as 316L stainless steel in simulated body fluids, but the corrosion rate is much lower than that of 316L stainless steel. The platelet adhesion behavior of NbC coating is significantly improved, which is expected to be an inert coating to improve the surface performance of naked 316L stainless steel. |