| LU Yu,LU Gang,SONG Tao,FENG Shu-juan,SU Wu,ZHAO Xia,XU Hong,LIU Li-hua.Study and Application of Photoinitiator for Thiol-olefin Polyorganosiloxane Large-core Optical Fiber Inner Coatings[J],46(3):138-142 |
| Study and Application of Photoinitiator for Thiol-olefin Polyorganosiloxane Large-core Optical Fiber Inner Coatings |
| Received:September 26, 2016 Revised:March 20, 2017 |
| View Full Text View/Add Comment Download reader |
| DOI：10.16490/j.cnki.issn.1001-3660.2017.03.021 |
| KeyWord:thiol-olefin functionalization polysiloxane UV-curing photoinitiator |
| Author | Institution |
| LU Yu |
School of Material Science and Engineering, Nanjing Tech University, Nanjing , China |
| LU Gang |
School of Material Science and Engineering, Nanjing Tech University, Nanjing , China |
| SONG Tao |
School of Material Science and Engineering, Nanjing Tech University, Nanjing , China |
| FENG Shu-juan |
Jiangsu Fasten Photonics Co., Ltd, Jiangyin , China |
| SU Wu |
Jiangsu Fasten Photonics Co., Ltd, Jiangyin , China |
| ZHAO Xia |
Jiangsu Fasten Group Co., Ltd, Jiangyin , China |
| XU Hong |
Jiangsu Fasten Group Co., Ltd, Jiangyin , China |
| LIU Li-hua |
Jiangsu Fasten Group Co., Ltd, Jiangyin , China |
|
| Hits: |
| Download times: |
| Abstract: |
| The work aims to prepare low-refractive index and low-loss large-core diameter optical fiber coating by performing screening test of photoinitiator. Thiol polydimethylsiloxane, vinyl silicone and photoinitiators were used to prepare polysiloxane UV-curing system functionalized by thiol-olefin. The effects of the system on refractive index, gel content, curing time and curing state were investigated. Then optimal photoinitiator was applied to field application test and fiber loss testing. In the five single-component photoinitiators, for coatings prepared by BP photoinitiation, the refractive index was 1.5795, optimal content 0.2% and fiber loss 7.1 dB/km; for coatings prepared by single-component Irgacure 184, the curing duration was 20 s, refractive index 1.5858, optimal content 1% and fiber loss 8.3 dB/km. In the four combined system, for coatings prepared by Irgacure1173+BP, the curing duration was 20 s, refractive index 1.5842, 1173: BP=2:1 and fiber loss 6.7 dB/km (the minimum). The addition of photoinitiator BP can reduce refractive index effectively in the polysiloxane UV-curing system functionalized by thiol-olefin. Coatings prepared by irgacure 184 are cured rapidly while coatings prepared by Irgacure1173+BP perform exhibits the lowest fiber loss. |