FAN Huan-ran,FAN Pu-cheng,ZHAO Wei,ZHAO Rui-chang.Study on the Characteristic of Inorganic Zinc Coating for Passive Containment[J],44(6):7-10 |
Study on the Characteristic of Inorganic Zinc Coating for Passive Containment |
Received:January 04, 2015 Revised:June 20, 2015 |
View Full Text View/Add Comment Download reader |
DOI:10.16490/j.cnki.issn.1001-3660.2015.06.002 |
KeyWord:passive containment inorganic zinc coating accident conditions |
Author | Institution |
FAN Huan-ran |
State Nuclear Power Technology R&D Centre, Beijing , China |
FAN Pu-cheng |
State Nuclear Power Technology R&D Centre, Beijing , China |
ZHAO Wei |
State Nuclear Power Technology R&D Centre, Beijing , China |
ZHAO Rui-chang |
State Nuclear Power Technology R&D Centre, Beijing , China |
|
Hits: |
Download times: |
Abstract: |
Objective To investigate the characteristics of IOZ coating for passive containment after design basis accident, so as to provide data support to the design of passive containment. Methods The physical environment of test was designed refer to the working condition of the DBA:specimen in the thermostatic oven heated to 160 ℃ until temperature uniformity, then immersed in 20 ℃ water. After cooling to room temperature, the samples were immersed in 100 ℃ water for 60 minutes. The impact of DBA for coating was studied, and the main characteristics of the IOZ coating were thermal conductivity, dry film thickness, surface morphology, adhesion, etc. Results After the test, the DFT of the coating was 70 ~130 microns, the adhesion was 8. 5 ~13. 5 MPa, and thermal conductivity increases by 6. 8% , but the surface morphology was unchanged. Conclusion After DBA, the DFT, surface morphology and adhesion was unchanged, but the thermal conductivity was edge up. |