| Study on Failure Behavior of Fluorinated Polyurethane-acrylic Coatings |
| Received:September 04, 2014 Revised:December 10, 2014 |
| View Full Text View/Add Comment Download reader |
| DOI： |
| KeyWord:fluorinated hydrophobic acrylic polyurethane coatings aging failure mechanism |
| Author | Institution |
| LI Sai |
Beihang University, Beijing , China |
| YANG Fei |
1. Beihang University, Beijing , China; 2. Wuhan Second Ship Design and Research Institute, Wuhan , China; |
| LI Wei-ping |
Beihang University, Beijing , China |
| LIU Hui-cong |
Beihang University, Beijing , China |
| ZHU Li-qun |
Beihang University, Beijing , China |
| WANG Xian-ming |
Marine Chemical Research Institute, Qingdao , China |
| NING Liang |
Marine Chemical Research Institute, Qingdao , China |
|
| Hits: |
| Download times: |
| Abstract: |
| Objective To investigate failure behaviors of fluorinated acrylic polyurethane coating in air environment and xenon accelerated aging test environment. Methods Water contact angle,attenuated total reflection-fourier transform infrared spectroscopy (ATR-FTIR),atomic force microscope(AFM) and Electrochemical Impedance Spectroscopy(EIS) were conducted to monitor the property variation of the coating. Results The results showed that coating contact angle decreased definitely in xenon accelerated aging test. ATR-FTIR spectra and AFM analysis indicated that the fluorine content decreased, while the oxygen content increased, and the coating surface roughness increased during the xenon lamp accelerated aging process. Coating resistance attenuated faster in xenon lamp accelerated aging test than in neutral salt spray test. Conclusion Photoaging began with a rupture of molecular chain, which led to a decrease of fluorine content, while coating resistance diminished along with time of aging. |