Modification of Nano-SiO2 and Its Effect on the Properties of Waterborne Polyurethane Resin Coating |
Received:February 26, 2013 Revised:March 28, 2013 |
View Full Text View/Add Comment Download reader |
DOI: |
KeyWord:nano-SiO2 modification particles size water polyurethane resin electrochemical corrosion resistance |
Author | Institution |
TANG Xiao-dong |
Institute of Molecular Engineering and Applied Chemistry, Anhui University of Technology, Ma'anshan , China |
ZHANG Zhen-hai |
Institute of Molecular Engineering and Applied Chemistry, Anhui University of Technology, Ma'anshan , China |
XU Li-ping |
Institute of Molecular Engineering and Applied Chemistry, Anhui University of Technology, Ma'anshan , China |
YANG Xing-liang |
Technique Center, Ma'anshan Iron & Steel Co. , Ltd. , Ma'anshan , China |
ZHANG Qian-feng |
Institute of Molecular Engineering and Applied Chemistry, Anhui University of Technology, Ma'anshan , China |
|
Hits: |
Download times: |
Abstract: |
In aqueous ethanol solution, the surface of nano-SiO2 was modified by silane coupling agent KH560 . And the particle sizes were measured. The effects of nano-SiO2 content, alcohol percentages and the modification agents on dispersity were discussed. The chromium-free passivation solution was made from the modified nano-SiO2 dispersions, water polyurethane resin and inorganic constituent compound, and it may be coated on the hot galvanized sheet . Corrosion resistances of nano-SiO2 modified polyurethane composite passivation film and unmodified polyurethane composite passivation film were characterized by the electrochemical Tafel polarization curves, AC impedances ( EIS) and the neutral salt spray tests. The results may show that compared with the latter the former corrosion resistance have been greatly improved. |