ZHOU Lei,PAN Ying-jun,XU Chao,PENG Jun-song,ZHANG Gai-lu.Study on Fe-6 . 5 %Si Steel Slice Prepared by PCVD[J],42(3):88-90 |
Study on Fe-6 . 5 %Si Steel Slice Prepared by PCVD |
Received:December 15, 2012 Revised:January 15, 2013 |
View Full Text View/Add Comment Download reader |
DOI: |
KeyWord:PCVD 6 . 5 % Si steel sheet siliconizing diffusion treatment |
Author | Institution |
ZHOU Lei |
Wuhan University of Science and Technology, Wuhan , China |
PAN Ying-jun |
Wuhan University of Science and Technology, Wuhan , China |
XU Chao |
Wuhan University of Science and Technology, Wuhan , China |
PENG Jun-song |
Wuhan University of Science and Technology, Wuhan , China |
ZHANG Gai-lu |
Wuhan University of Science and Technology, Wuhan , China |
|
Hits: |
Download times: |
Abstract: |
Fe-6 . 5 % Si high silicon steel sheet was available after silicon was deposited on the surface of plain pure steel sheet with 0 . 2 mm heavy through PCVD, then treated at a high temperature. Analyzed the impact of deposition process parameters on the surface of the silicon content by orthogonal test, the relationship between diffusion parameters and the cross-sectional distribution of silicon content was studied. The results show that 40 . 5 % of the surface silicon is obtained by the 10 % SiH4and 90 % Ar as the seepage source, 500 ℃ deposition for 20 min. Meeting the requirements of Fe-6 . 5 % Si high silicon steel sheet is obtained in the protection of industrial pure H2at 1050 ℃ insulating for 60 min. |