GE Pei-lin,GE Pei-lin,GE Pei-lin,GE Pei-lin,GE Pei-lin.The Influence of Prior Plasma Nitriding on the Adhesion Strength of CrTiAlN Coating Formed on H13 Steel[J],(2):79-81 |
The Influence of Prior Plasma Nitriding on the Adhesion Strength of CrTiAlN Coating Formed on H13 Steel |
Received:November 24, 2011 Revised:April 20, 2012 |
View Full Text View/Add Comment Download reader |
DOI: |
KeyWord:plasma nitriding magnetron sputtering nitrided layer CrTiAlN coating adhesion strength |
Author | Institution |
GE Pei-lin |
Research Institute of Surface Engineering, Taiyuan University of Technology, Taiyuan , China |
GE Pei-lin |
Research Institute of Surface Engineering, Taiyuan University of Technology, Taiyuan , China |
GE Pei-lin |
Institute of Materials Engineering, Ningbo University of Technology, Ningbo , China |
GE Pei-lin |
Institute of Materials Engineering, Ningbo University of Technology, Ningbo , China |
GE Pei-lin |
Institute of Materials Engineering, Ningbo University of Technology, Ningbo , China |
|
Hits: |
Download times: |
Abstract: |
A nitride layer was first formed on H13 steel samples by plasma nitriding and then a CrTiAlN coating was prepared on the surface of nitrided and non-nitrided H13 steels using closed field unbalanced magnetron sputter ion plating. The adhesion strength, the microstructure and phase structure of the film were compared between nitrided and non-nitrided H13.The results show that the substrate hardness increases after plasma nitridation and exhibits a gradient hardness transition. The complex treatment of plasma nitridation and CrTiAlN coatings could increase the adhesion strength significantly. |