DU Zuo-juan,ZHOU Ding,HUANG Xiao-zhong,WANG Chao-ying,DUAN Xi-dong.Preparation and Performance of T-ZnOw Coated Fe Composite Powder[J],39(6):59-62 |
Preparation and Performance of T-ZnOw Coated Fe Composite Powder |
Received:August 18, 2010 Revised:December 10, 2010 |
View Full Text View/Add Comment Download reader |
DOI: |
KeyWord:composite powder chemical coated T-ZnOw Fe magnetic characteristics |
Author | Institution |
DU Zuo-juan |
School of Physical Science and Technology, Central South University, Changsha , China |
ZHOU Ding |
School of Physical Science and Technology, Central South University, Changsha , China |
HUANG Xiao-zhong |
School of Physical Science and Technology, Central South University, Changsha , China |
WANG Chao-ying |
School of Physical Science and Technology, Central South University, Changsha , China |
DUAN Xi-dong |
School of Physical Science and Technology, Central South University, Changsha , China |
|
Hits: |
Download times: |
Abstract: |
T-ZnOw coated Fe(OH)3composite powders were prepared in the basic system by the chemical coating method using ammonia as the precipitating agent. Fe/ T-ZnOw composite powder was obtained through hydrogen reduction at 600℃ . The powder was characterized by XRD,SEM and EDX. The results show that there are metal iron phase and T-ZnOw phase in the composite powder. The tetrapod of T-ZnOw wasintact and coated fully by iron particles.Some iron particles, shperical particle about 3μm, were scattered outside the surface of T-ZnOw. Saturation magnetization and coercivity of the composite powder were measured by the VSM, respectively 32.10 emu/g and 140.5 Oe. |