Hot Corrosion Behavior of an Ion Plating NiCrAIY Coating with Alununizing |
Received:February 25, 2008 Revised:August 10, 2008 |
View Full Text View/Add Comment Download reader |
DOI: |
KeyWord:Aluminizing Ion plating Hot corrosion NiCAIY |
Author | Institution |
REN Xin |
Department of Materials Science and Engineering, Liaoning Technical University, Fuxin , China |
|
Hits: |
Download times: |
Abstract: |
A NiCrAIY coating was deposited on a Ni-based superalloy by ion plating. Post-aluminizing was performed on the coating to improve the corresponding high-temperature properties. Hot corrosion behaviors in the presence of 750/o Na2S04 +250/o NaCl film at 850℃ of the coatings with and without aluminizing have been investigated. In 250/o NaCl +750/o Na2S04 molten salt at 850℃ , Cr203 scale formed on NiCrAIY coating at 40h, while at the same time a single layer of a-Al203 scale formed on the coating with post-aluminizing. The main oxide of Al203 remained on the surface of the coating with post-aluminizing, which obviously increased the resistance to hot corrosion of the coating. |