HU Shi-ju,SHI Hai-fang,2hi_chao.Study on Microstructures and Properties of Al203/Cu Composite Material by Internal Oxidation of Deeply Aluminized Pure Copper Matrix[J],37(3):33-35,64 |
Study on Microstructures and Properties of Al203/Cu Composite Material by Internal Oxidation of Deeply Aluminized Pure Copper Matrix |
Received:February 20, 2008 Revised:June 10, 2008 |
View Full Text View/Add Comment Download reader |
DOI: |
KeyWord:Deeply aluminized Internal oxidation Wear resistance Thermal fatigue Pure copper |
Author | Institution |
HU Shi-ju |
Fuxin Campus of Liaoning Radio and TV University, Fuxin , China |
SHI Hai-fang |
Department of Material Science and Engineering, Liaoning Technical University, Fuxin , China |
2hi_chao |
Department of Material Science and Engineering, Liaoning Technical University, Fuxin , China |
|
Hits: |
Download times: |
Abstract: |
To improve the heat resistance and wear resistance of coppery elements, the Al203/Cu composite material was prepared by intemal oxidation of deeply aluminized pure copper matrix. The microstructures and properties of the composite material were studied. The results show that the grain-abrasion resistance and adhesive wear resistance is 1. 85 times and 9. 4 times that of copper respectively; the thermal fatigue resistance of the composite is higher than that of copper, the weightlessness of thermal fatigue sample is 0. 880/o of that of copper. The specialty makes the Al203/Cu composite material by internal oxidation of deeply aluminized pure copper matrix is more fine to be the diathermanous copper material of metallurgical equipment in the high temperature service condition than the ageing and solution alloy of aluminized deeply pure copper. |