KANG Shu-mei,WANG Lin,LI Cheng-wei,CHEN Hua.Study on Corrosion Resistance of Electroless Ni-P Alloy in the Acidic Solution at Middle Temperature[J],37(3):27-29 |
Study on Corrosion Resistance of Electroless Ni-P Alloy in the Acidic Solution at Middle Temperature |
Received:March 15, 2008 Revised:June 10, 2008 |
View Full Text View/Add Comment Download reader |
DOI: |
KeyWord:Electroless plating Ni-P alloy Corrosion resistance Heat treatment |
Author | Institution |
KANG Shu-mei |
School of Materials Science and Engineering, Liaoning University of Science and Technology, Liaoning , China |
WANG Lin |
School of Materials Science and Engineering, Liaoning University of Science and Technology, Liaoning , China |
LI Cheng-wei |
School of Materials Science and Engineering, Liaoning University of Science and Technology, Liaoning , China |
CHEN Hua |
Medium and Heavy Plate Plant Angang Steel Company Limited, Anshan , China |
|
Hits: |
Download times: |
Abstract: |
To improve the corrosion resistance of electroless Ni-P alloy, used Q235 steel as substrates, the effect of process parameters on the corrosion resistance of the nickel-plating was studied in the acidic solution at middle temperature by the orthogonal experimental method. By the range analysis, the best conditions were determined:process for the best prescription: molar ratio of Nj2+ and H2P02 - is 0. 48 ; compound complexing agent of lactic acid is 15mL/L; propionic acid is 5mL/L; accelerator NaF is 0.4 g/L; Stabilizer thiourea is Img/L; buffer sodium acetate is 16.5g/L; surfactants lauryl sodium sulfonate is lOmg/L; pH value 5.2; plating time is 2h; heat treatment temperature is 500℃. On the condition, the corrosion current is 2. 166 x 10 -5A and the corrosion resistance is improved. |