| WANG Yan-feng,LI Zheng-xian,HUA Yun-feng,WANG Bao-yun,DU Ji-hong.Influence of C Incorporation Modes on the TiAlSiN Coating' s Microstructure and Properties[J],42(4):32-34,38 |
| Influence of C Incorporation Modes on the TiAlSiN Coating' s Microstructure and Properties |
| Received:April 26, 2013 Revised:May 20, 2013 |
| View Full Text View/Add Comment Download reader |
| DOI： |
| KeyWord:C incorporatin TiAlSiN hard coating microstructure wearing properties |
| Author | Institution |
| WANG Yan-feng |
Northwest Institute for Nonferrous Metal Research, Xi'an , China |
| LI Zheng-xian |
Northwest Institute for Nonferrous Metal Research, Xi'an , China |
| HUA Yun-feng |
Northwest Institute for Nonferrous Metal Research, Xi'an , China |
| WANG Bao-yun |
Northwest Institute for Nonferrous Metal Research, Xi'an , China |
| DU Ji-hong |
Northwest Institute for Nonferrous Metal Research, Xi'an , China |
|
| Hits: |
| Download times: |
| Abstract: |
| A combination of arc and magnetron sputtering deposition technology was used to synthesize the C / TiAlSiN hard coatings with different C incorporation modes on the high-speed steel substrates. The coating ' s composition, microstructure, microhardness and wearing properties were studied and compared with that of TiAlSiN coatings which has none-C incorporation. It was found that the coatings had different microstructure and properties with different C incorporation mode. The incorporation of C during the TiAlSiN coating synthesis was very useful to optimize the coating's microstructure and micro hardness,and also good for its wearing properties. |