| LIU Xin-hu,SUN Cai-yun,WANG Qing-hui,HAN Jie.Mechanism of Compound Inhibitors in Natural Sea Water with Methods of Surface Analysis[J],42(3):19-22 |
| Mechanism of Compound Inhibitors in Natural Sea Water with Methods of Surface Analysis |
| Received:December 13, 2012 Revised:January 20, 2013 |
| View Full Text View/Add Comment Download reader |
| DOI： |
| KeyWord:surface analysis corrosion and scale mechanism synergy natural seawater |
| Author | Institution |
| LIU Xin-hu |
College of Light Industry,Hebei United University,Tangshan , China |
| SUN Cai-yun |
College of Light Industry,Hebei United University,Tangshan , China |
| WANG Qing-hui |
College of Light Industry,Hebei United University,Tangshan , China |
| HAN Jie |
College of Light Industry,Hebei United University,Tangshan , China |
|
| Hits: |
| Download times: |
| Abstract: |
| The synergistic mechanism of inhibitor including molybdate, organic phosphate,PESA and Zn2+on the metal surface was explored with methods of EDS,XPS and SEM. EDS analysis showed that Fe content was increased from 62 . 68 % to 96 . 80 % and the calcium content was decreased from 34 . 56 % to 0 . 10 % by comparing to the blank seawater specimens with adding inhibitors specimen. So the crevice corrosion under the scale was slowed. XPS analysis showed that compound inhibitor was added so that coverage rate on the metal surface of the iron oxide film was higher and denser and calcium was not found, which was consistent with the test results of the EDS. SEM analysis showed that there was no corrosion trace and no mechanical scratch in solution adding composite formulations; Crystals of calcium carbonate became from the most stable structure of calcite scale layer to unstable dispersion vaterite. |