| WANG Zhao-hua,YANG Rui-song,SUN Xiao-ming,LIU Yuan-hong.The Research on the Phosphating Film Closed by Copper with Replacement Plating[J],42(1):98-100 |
| The Research on the Phosphating Film Closed by Copper with Replacement Plating |
| Received:September 21, 2012 Revised:November 15, 2012 |
| View Full Text View/Add Comment Download reader |
| DOI： |
| KeyWord:phosphating film replacement plating copper close |
| Author | Institution |
| WANG Zhao-hua |
Material Corrosion and Protection Key Laboratory of Sichuan Province, Sichuan University of Science and Engineering, Zigong , China |
| YANG Rui-song |
Material Corrosion and Protection Key Laboratory of Sichuan Province, Sichuan University of Science and Engineering, Zigong , China |
| SUN Xiao-ming |
Material Corrosion and Protection Key Laboratory of Sichuan Province, Sichuan University of Science and Engineering, Zigong , China |
| LIU Yuan-hong |
Sichuan Kehone Oil & Gas Enginering Co. , Ltd. , Chengdu , China |
|
| Hits: |
| Download times: |
| Abstract: |
| The replacement copper plating on the phosphating film was carried out in copper sulfate solution. The results showed that it爷 s feasible to plate copper on phosphating film. After plating the strength and the corrosion resistance of the as-prepared phosphating film can be increased. The time of the plating should be short and the concentration of the copper sulfate should be low. The suggested experiment parameters are listed as follows: the concentration of copper sulfate is 2 % , the temperature is room temperature and the time is 3 ~ 5 min. |