皮志超,宋宜强,闫江涛,李柱祥,胡水莲,周飞.30CrMnSiA钢表面镉镀层化学转化膜的电化学特性[J].表面技术,2023,52(6):307-318.
PI Zhi-chao,SONG Yi-qiang,YAN Jiang-tao,LI Zhu-xiang,HU Shui-lian,ZHOU Fei.Electrochemical Characteristics of Chemical Conversion Film of Cadmium Coating on 30CrMnSiA Steel Surface[J].Surface Technology,2023,52(6):307-318 |
| 30CrMnSiA钢表面镉镀层化学转化膜的电化学特性 |
| Electrochemical Characteristics of Chemical Conversion Film of Cadmium Coating on 30CrMnSiA Steel Surface |
| |
| DOI：10.16490/j.cnki.issn.1001-3660.2023.06.027 |
| 中文关键词: 镉镀层 化学转化膜 腐蚀 电化学 阻抗 极化曲线 |
| 英文关键词:cadmium coating chemical conversion film corrosion electrochemical impedance polarization curve |
| 基金项目:上海航翼高新技术发展研究院有限公司合作项目(1005–KFA20890) |
|
|
| Author | Institution |
| PI Zhi-chao | State Key Laboratory of Mechanics and Control for Aerospace Structures, Nanjing University of Aeronautics and Astronautics, Nanjing 210016, China;State-owned Wuhu Machinery Factory, Anhui Wuhu 241007, China |
| SONG Yi-qiang | State Key Laboratory of Mechanics and Control for Aerospace Structures, Nanjing University of Aeronautics and Astronautics, Nanjing 210016, China |
| YAN Jiang-tao | State Key Laboratory of Mechanics and Control for Aerospace Structures, Nanjing University of Aeronautics and Astronautics, Nanjing 210016, China |
| LI Zhu-xiang | State-owned Wuhu Machinery Factory, Anhui Wuhu 241007, China |
| HU Shui-lian | State-owned Wuhu Machinery Factory, Anhui Wuhu 241007, China |
| ZHOU Fei | State Key Laboratory of Mechanics and Control for Aerospace Structures, Nanjing University of Aeronautics and Astronautics, Nanjing 210016, China |
|
| 摘要点击次数: |
| 全文下载次数: |
| 中文摘要: |
| 目的 通过研究镉镀层绿色化学转化膜的电化学性能，获得镉镀层最佳绿色化学钝化工艺。方法 采用无氰镀镉工艺，在30CrMnSiA钢表面电镀镉。采用植酸和钼酸钠在镉镀层表面进行绿色钝化处理，构建复合化学转化膜。通过研究钼酸钠浓度、处理时间和植酸浓度对绿色钝化处理镀镉层在质量分数为3.5%的NaCl溶液中电化学性能的影响，获得最佳的镀镉层绿色钝化工艺。结果 在处理时间为10 min、植酸的质量分数为1.0%的条件下，当钼酸钠的质量分数增至3%时，开路电压先从−0.741 9 V增至−0.739 7 V后，再降至−0.761 1 V，电荷转移电阻Rct从2.34 kΩ.cm2增至8.79 kΩ.cm2，腐蚀抑制率从72.9%增至92.8%，自腐蚀电流密度Jcorr从81.47 μA/cm2降至最低值(6.887 2 μA/cm2)。当钼酸钠和植酸的质量分数分别为2.0%和1.0%时，随着处理时间的延长，开路电压从−0.755 9 V增至−0.729 5 V，Rct先增至6.68 kΩ.cm2，然后降至5.28 kΩ.cm2，自腐蚀电流密度从16.26 μA/cm2降至4.527 μA/cm2。当钼酸钠的质量分数为2.0%、处理时间为10 min时，随着植酸浓度的增加，试样的开路电压从−0.739 3 V降至−0.756 1 V，Rct先增至6.68 kΩ.cm2，然后降低，自腐蚀电流密度Jcorr呈现先降至最小值后再增大的趋势。结论 与镉镀层相比，经化学转化膜处理后试样表现为高的开路电压、大的电荷转移电阻和低的自腐蚀电流。得到了耐蚀性好且成本较低的镉镀层表面绿色钝化工艺，钼酸钠和植酸的质量分数分别为2.0%和1.0%，处理时间为10 min。 |
| 英文摘要: |
| The work aims to obtain the best green chemical passivation process of cadmium plating layers by studying the electrochemical properties of green chemical conversion films of cadmium plating layers. The cadmium coatings were electroplated on the surface of 30CrMnSiA steel through the cyanide-free cadmium plating process, and the green passivation treatment was performed on the cadmium coating on the surface of 30CrMnSiA steel in the solution containing phytic acid and sodium molybdate, then a composite chemical conversion film was constructed on the surface of the cadmium layer. After the effects of sodium molybdate concentration, phytic acid concentration and treatment time on the electrochemical properties of the green passivation cadmium plating layer were studied in 3.5wt.% NaCl solution, the green chemical passivation process of cadmium plating layer was obtained. When the treatment time was 10 min and the concentration of phytic acid was 1.0wt.%, with an increase of 3% in the concentration of sodium molybdate, the open circuit voltage value of the sample first increased from −0.741 9 V to −0.739 7 V, and then decreased to −0.761 1 V. And the charge transfer resistance Rct value and corrosion inhibition rate also increased from 2.34 kΩ.cm2 to 8.79 kΩ.cm2 and 72.9% to 92.8%, respectively, while its self-corrosion current density Jcorr first decreased from 81.47 μA/cm2 to 6.887 μA/cm2. If the concentrations of sodium molybdate and phytic acid were 2.0wt.% and 1.0wt.%, respectively, with the increase of treatment time, the open circuit voltage value of the sample increased from −0.755 9 V to −0.729 5 V. Its Rct value first increased to 6.68 kΩ.cm2, and then decreased to 5.28 kΩ.cm2, while its self-corrosion current density decreased from 16.26 μA/cm2 to 4.527 μA/cm2. When the concentration of sodium molybdate was 2.0wt.% and the treatment time was 10 min, with the increase of phytic acid concentration, the open circuit voltage value of the sample decreased from −0.739 3 V to −0.756 1 V. And its Rct value first increased to 6.68 kΩ.cm2, and then decreased, while the self-corrosion current density Jcorr value first decreased to the minimum value and then increased. Compared with the cadmium coating, the samples treated with the chemical conversion coating have higher open circuit voltage, larger charge transfer resistance and lower self-corrosion current. The green passivation process for the surface of cadmium coating has good corrosion resistance and low cost concentration. The sodium molybdate and phytic acid are 2.0wt.% and 1.0wt.%, respectively, and the treatment time is 10 min. |