卞达,倪自丰,钱善华,王永光,赵永武.GO-TiO2对磷酸盐粘结涂层耐磨损性能的影响[J].表面技术,2021,50(4):56-61.
BIAN Da,NI Zi-feng,QIAN Shan-hua,WANG Yong-guang,ZHAO Yong-wu.Influence of GO-TiO2 on Wear Resistance Properties of Phosphate Bonded Coating[J].Surface Technology,2021,50(4):56-61 |
| GO-TiO2对磷酸盐粘结涂层耐磨损性能的影响 |
| Influence of GO-TiO2 on Wear Resistance Properties of Phosphate Bonded Coating |
| 投稿时间：2021-01-15 修订日期：2021-03-16 |
| DOI：10.16490/j.cnki.issn.1001-3660.2021.04.004 |
| 中文关键词: 氧化石墨烯 粘结涂层 磨损 裂纹 界面结合 |
| 英文关键词:graphene oxide bonded coating wear crack interfacial adhesive |
| 基金项目:国家自然科学基金(51675232);江苏省自然科学基金(BK20190611);中国博士后基金(2020M681482) |
| 作者 | 单位 |
| 卞达 | 江南大学 机械学院江苏省先进食品制造装备技术重点实验室，江苏 无锡 214122 |
| 倪自丰 | 江南大学 机械学院江苏省先进食品制造装备技术重点实验室，江苏 无锡 214122 |
| 钱善华 | 江南大学 机械学院江苏省先进食品制造装备技术重点实验室，江苏 无锡 214122 |
| 王永光 | 苏州大学 机电工程学院，江苏 苏州 215006 |
| 赵永武 | 江南大学 机械学院江苏省先进食品制造装备技术重点实验室，江苏 无锡 214122 |
|
| Author | Institution |
| BIAN Da | College of Mechanical Engineering, Jiangsu Key Laboratory of Advanced Food Manufacturing Equipment and Technology, Jiangnan University, Wuxi 214122, China |
| NI Zi-feng | College of Mechanical Engineering, Jiangsu Key Laboratory of Advanced Food Manufacturing Equipment and Technology, Jiangnan University, Wuxi 214122, China |
| QIAN Shan-hua | College of Mechanical Engineering, Jiangsu Key Laboratory of Advanced Food Manufacturing Equipment and Technology, Jiangnan University, Wuxi 214122, China |
| WANG Yong-guang | College of Mechanical Engineering, Soochow University, Suzhou 215006, China |
| ZHAO Yong-wu | College of Mechanical Engineering, Jiangsu Key Laboratory of Advanced Food Manufacturing Equipment and Technology, Jiangnan University, Wuxi 214122, China |
|
| 摘要点击次数: |
| 全文下载次数: |
| 中文摘要: |
| 目的 提高磷酸盐粘结涂层的耐磨损性能。方法 以3-氨基丙基三乙氧基硅烷为纽带，制备氧化石墨烯-二氧化钛复合材料(GO-TiO2)，并作为增强相加入涂层中。通过SEM和FTIR，对GO-TiO2的微观结构和官能团进行表征，采用维氏硬度计对涂层显微硬度进行测量，利用摩擦磨损试验机测试涂层的摩擦学行为，采用白光干涉仪和SEM对涂层磨痕微观结构进行表征。结果 二氧化钛和氧化石墨烯通过化学键连接在一起，且由于二氧化钛的存在，氧化石墨烯表面变得粗糙，从而加强机械啮合作用，提高了涂层其他组分与氧化石墨烯的界面结合力。随着GO-TiO2的加入，涂层的显微硬度增加。未添加GO-TiO2涂层的显微硬度为207.4HV0.3，添加1.0%(质量分数)GO-TiO2时，涂层的显微硬度增加至260.4 HV0.3。涂层的摩擦因数随着GO-TiO2的加入稍微降低，而涂层的耐磨损性能显著增加。未添加GO-TiO2涂层的摩擦因数为0.51左右，磨损率为2.17´10–4 mm3/(N.m)，当添加1.0% GO-TiO2时，涂层摩擦因数和磨损率分别降低至0.45和0.51´10–4 mm3/(N.m)。结论 涂层磨损主要是由脆性剥落引起的，而且GO-TiO2的添加并未改变涂层磨损机制。GO-TiO2通过抑制裂纹的拓展，提高了涂层的耐磨损性能。 |
| 英文摘要: |
| To improve the wear resistance of phosphate bonded coating, graphene oxide-titanium dioxide (GO-TiO2) was prepared with 3-Aminopropyltriethoxysilane as bridge and added into phosphate bonded coating as the reinforcement. SEM and FTIR was used to study the microstructure and phase of GO-TiO2. In addition, the hardness and triboligical behavior were tested with Vickers hardness tester and a tribometer, respectively. Besides, the microstructure of worn surface was studied by SEM and white light interferometer. The results show that TiO2 is grafted to GO through chemical bonds. Besides, the surface of GO becomes rough with the presence of TiO2, which can strengthen mechanical joggle and improve the interfacial adhesive between GO and the coating matrix. The hardness of the coating is improved with the introduction of GO-TiO2. The hardness of the coating without GO-TiO2 is 207.4 HV0.3, while the hardess reaches to 260.4 HV0.3 with the introduction of 1.0% GO-TiO2. In addition, the friction coefficient slightly decreases with GO-TiO2. However, the wear resistance of the coating is obviously increase. The friction coefficient and wear rate of the coating without GO-TiO2 are 0.51 and 2.17´10–4 mm3/(N.m), respectively. When added 1.0% GO-TiO2, the friction coefficient and wear rate decrease to 0.45 and 0.51´10–4 mm3/(N.m), respectively. The wear is mainly attributed to brittle delamination, and the wear resistance of coating is improved because cracks propagation is inhibited by GO-TiO2. |