王振尧,王彬彬,曹公望,柯伟.盐沉积条件下CO2对LY12铝合金大气腐蚀的影响[J].表面技术,2017,46(4):79-83.
WANG Zhen-yao,WANG Bin-bin,CAO Gong-wang,KE Wei.Effects of CO2 on Salt Deposition-induced Atmospheric Corrosion of Alu-minum Alloy LY12[J].Surface Technology,2017,46(4):79-83 |
| 盐沉积条件下CO2对LY12铝合金大气腐蚀的影响 |
| Effects of CO2 on Salt Deposition-induced Atmospheric Corrosion of Alu-minum Alloy LY12 |
| 投稿时间：2016-09-18 修订日期：2017-04-20 |
| DOI：10.16490/j.cnki.issn.1001-3660.2017.04.014 |
| 中文关键词: LY12铝合金 大气腐蚀 沉积盐 CO2 产物分析 模拟腐蚀试验 |
| 英文关键词:aluminum alloy LY12 atmospheric corrosion salt deposition CO2 product analysis simulated corrosion test |
| 基金项目:国家自然科学基金项目（51131007，51671197） |
| 作者 | 单位 |
| 王振尧 | 中国科学院金属研究所，沈阳 110016 |
| 王彬彬 | 中国科学院金属研究所，沈阳 110016 |
| 曹公望 | 中国科学院金属研究所，沈阳 110016 |
| 柯伟 | 中国科学院金属研究所，沈阳 110016 |
|
| Author | Institution |
| WANG Zhen-yao | Institute of Metal Research, Chinese Academy of Sciences, Shenyang 110016, China |
| WANG Bin-bin | Institute of Metal Research, Chinese Academy of Sciences, Shenyang 110016, China |
| CAO Gong-wang | Institute of Metal Research, Chinese Academy of Sciences, Shenyang 110016, China |
| KE Wei | Institute of Metal Research, Chinese Academy of Sciences, Shenyang 110016, China |
|
| 摘要点击次数: |
| 全文下载次数: |
| 中文摘要: |
| 目的 研究在有/无CO2存在的恒温恒湿条件下，表面有沉积盐的LY12铝合金的大气腐蚀行为与腐蚀机理，搞清CO2对其大气腐蚀的影响。方法 将LY12铝合金表面分别沉积不同浓度的NaCl和MgCl2，分别进行通/不通CO2的恒温恒湿实验，借助扫描电镜（SEM/EDS）、X射线衍射（XRD）和X光电子能谱（XPS）等表面技术以及腐蚀失重分析方法，研究盐沉积条件下CO2对LY12铝合金大气腐蚀的影响。结果 在试验条件下，MgCl2造成的LY12铝合金腐蚀都以点蚀为主，失重高于NaCl造成的。以MgCl2为介质时，主要腐蚀产物都为(Mg1–xAlx(OH)2)x+(Cl–, CO2–)xmH2O（简写为LDH）；以NaCl为介质时，主要腐蚀产物都为Al2O3或Al(OH)3。两种介质的腐蚀产物都出现了Cu元素的富集。结论 无论是否存在CO2 ，Mg元素都参与了腐蚀产物的形成。合金元素Cu的存在及其富集，是造成CO2对纯铝和LY12铝合金腐蚀行为不同影响的主要因素。 |
| 英文摘要: |
| The work aims to study effects of CO2 on atmospheric corrosion as well as atmospheric corrosion behavior and corrosion mechanism of LY12 aluminum alloy with salt deposits on the surface in constant temperature and humidity with/without CO2. Different concentrations of NaCl and MgCl2 were deposited on aluminum alloy LY12 and constant temperature and humidity test with/without CO2. Effects of CO2 on salt deposition-induced atmospheric corrosion of aluminum alloy LY12 were studied by means of SEM/EDS, XRD and XPS. In the test conditions, pitting was dominant in MgCl2-induced atmospheric corrosion of aluminum alloy LY12, and MgCl2-induced weight loss was higher than that induced by NaCl. (Mg1–xAlx(OH)2)x+(Cl–, CO2–)xmH2O (LDH) was major corrosion product in the MgCl2-induced corrosion process. However, Al2O3 or Al(OH)3 was major corrosion product under the influence of NaCl. Cu enriched in corrosion products of both mediums. Whether CO2 is present or not, Mg in MgCl2 takes part in forming corrosion products. Different effects of CO2 on corrosion behavior of pure Al and LY12 are mainly attributed to the presence or enrichment of Cu. |