邓乔元,张腾飞,武冰洁,李仕莎,冷永祥,黄楠.类金刚石薄膜在人工关节摩擦配副表面改性的应用[J].表面技术,2016,45(5):1-7.
DENG Qiao-yuan,ZHANG Teng-fei,WU Bing-jie,LI Shi-sha,LENG Yong-xiang,HUANG Nan.Diamond-like Carbon Film and Its Application on Articular Surface of Artificial Joint for Increasing Wear Resistance[J].Surface Technology,2016,45(5):1-7
类金刚石薄膜在人工关节摩擦配副表面改性的应用
Diamond-like Carbon Film and Its Application on Articular Surface of Artificial Joint for Increasing Wear Resistance
投稿时间:2016-01-08  修订日期:2016-05-20
DOI:10.16490/j.cnki.issn.1001-3660.2016.05.001
中文关键词:  人工关节  金属离子  生物薄膜  类金刚石薄膜  蛋白质
英文关键词:artificial joint  metal ion  biofilm  diamond-like carbon film  protein
基金项目:国家自然科学基金(31570958, 81271953)
作者单位
邓乔元 西南交通大学 材料科学与工程学院,成都 610031 
张腾飞 西南交通大学 材料科学与工程学院,成都 610031 
武冰洁 西南交通大学 材料科学与工程学院,成都 610031 
李仕莎 西南交通大学 材料科学与工程学院,成都 610031 
冷永祥 西南交通大学 材料科学与工程学院,成都 610031 
黄楠 西南交通大学 材料科学与工程学院,成都 610031 
AuthorInstitution
DENG Qiao-yuan School of Materials Science and Engineering, Southwest Jiaotong University, Chengdu 610031, China 
ZHANG Teng-fei School of Materials Science and Engineering, Southwest Jiaotong University, Chengdu 610031, China 
WU Bing-jie School of Materials Science and Engineering, Southwest Jiaotong University, Chengdu 610031, China 
LI Shi-sha School of Materials Science and Engineering, Southwest Jiaotong University, Chengdu 610031, China 
LENG Yong-xiang School of Materials Science and Engineering, Southwest Jiaotong University, Chengdu 610031, China 
HUANG Nan School of Materials Science and Engineering, Southwest Jiaotong University, Chengdu 610031, China 
摘要点击次数:
全文下载次数:
中文摘要:
      关节置换术是目前治疗关节疾病最直接、有效的手段,随着国民经济的增长,人工关节在我国的需求量不断增加。介绍了常见人工关节的类型及特点,以及目前用于提高人工关节摩擦副表面耐磨损性及耐腐蚀性的方法,通过比较发现,类金刚石(DLC)薄膜在提高人工关节耐磨损、耐腐蚀性能方面具有更好的应用前景。阐述了 DLC 薄膜结构、性能及其制备方法,并结合目前 DLC 薄膜在人工关节摩擦配副表面改性中应用所面临的主要问题,介绍了目前用于降低 DLC 薄膜内应力、增加 DLC薄膜/基体结合力的方法。最后,针对 DLC 薄膜应用于人工关节摩擦配副表面改性中存在的缝隙腐蚀及结合失效问题,并结合人工关节体内服役环境特点,提出了利用金属离子催化人工关节摩擦配副表面吸附蛋白的变性、分解,形成致密生物薄膜,对 DLC 薄膜的磨痕和缺陷进行修复的思想,展望了新型 DLC 薄膜在人工关节表面改性中的应用前景。
英文摘要:
      Arthroplasty is the most effective method for the treatment of joint disease in clinical practice, and there are increasing needs for artificial joints with the development of national economy. There are three types of artificial joints in clinical practice. Lots of methods have been used to enhance the wear and corrosion resistance of artificial joints. Diamond-like carbon (DLC) film has low friction coefficient, high wear resistance and good biocompatibility, which has been used to improve the wear and corrosion resistance of artificial joints. But the clinical use of DLC coated artificial joint is unsatisfying. This paper discussed the reasons for DLC failure in vivo. Metal doping DLC film or multilayer DLC film could lower the internal stress, improve the adhesion and postpone the DLC film failure. Concerning the service environment of artificial joints, the crevice corrosion and adhesion of DLC film, we proposed to control the formation of biofilm on the surface of the artificial joints through the use of metal ions to promote protein denaturation and decomposition. And this biofilm could prevent corrosion medium (Cl-, PO43-) from penetrating into the interface of film and substrate. So the crevice and interface corrosion would be restrained. And the lifetime of DLC film would be prolonged.
查看全文  查看/发表评论  下载PDF阅读器
关闭

关于我们 | 联系我们 | 投诉建议 | 隐私保护 | 用户协议

您是第20721099位访问者    渝ICP备15012534号-3

版权所有:《表面技术》编辑部 2014 surface-techj.com, All Rights Reserved

邮编:400039 电话:023-68792193传真:023-68792396 Email: bmjs@surface-techj.com

渝公网安备 50010702501715号