张曼,陈朝轶,李军旗,赵聪,杨夏琼.铝酸钠溶液中 Na2 S 对 Q235 钢腐蚀的影响[J].表面技术,2015,44(8):86-91,129.
ZHANG Man,CHEN Chao-yi,LI Jun-qi,ZHAO Cong,YANG Xia-qiong.Effect of Na2S in Sodium Aluminate Solution on the Corrosion Behavior of Q235 Steel[J].Surface Technology,2015,44(8):86-91,129 |
| 铝酸钠溶液中 Na2 S 对 Q235 钢腐蚀的影响 |
| Effect of Na2S in Sodium Aluminate Solution on the Corrosion Behavior of Q235 Steel |
| 投稿时间：2015-04-22 修订日期：2015-08-20 |
| DOI：10.16490/j.cnki.issn.1001-3660.2015.08.016 |
| 中文关键词: 铝酸钠溶液 Q235 Na2S 质量浓度 腐蚀时间 腐蚀速率 极化曲线 |
| 英文关键词:sodium aluminate solution Q235 Na2 S concentration corrosion time corrosion rate polarization curve |
| 基金项目:国家自然科学基金资助项目(51264006,51474079, 51464008);贵州省教育厅项目(黔教合重大专项字(2012)0002);贵州省校合作项目(LH[2014]7609) |
|
|
| Author | Institution |
| ZHANG Man | 1. College of Materials and Metallurgy, Guizhou University, Guiyang 550025, China;2. Guizhou Province Key Laboratory of Metallurgical Engineering and Process Energy Saving, Guiyang 550003, China |
| CHEN Chao-yi | 1. College of Materials and Metallurgy, Guizhou University, Guiyang 550025, China;2. Guizhou Province Key Laboratory of Metallurgical Engineering and Process Energy Saving, Guiyang 550003, China |
| LI Jun-qi | Guizhou Province Key Laboratory of Metallurgical Engineering and Process Energy Saving, Guiyang 550003, China |
| ZHAO Cong | 1. College of Materials and Metallurgy, Guizhou University, Guiyang 550025, China;2. Guizhou Province Key Laboratory of Metallurgical Engineering and Process Energy Saving, Guiyang 550003, China |
| YANG Xia-qiong | 1. College of Materials and Metallurgy, Guizhou University, Guiyang 550025, China;2. Guizhou Province Key Laboratory of Metallurgical Engineering and Process Energy Saving, Guiyang 550003, China |
|
| 摘要点击次数: |
| 全文下载次数: |
| 中文摘要: |
| 目的 研究在含 S2-的铝酸钠溶液中 Q235 钢的腐蚀行为。 方法 模拟生产条件配制种分母液,采用盐雾腐蚀实验与 SEM 和 EDS 分析技术,结合腐蚀质量损失动力学方程与极化曲线,研究 Na2S 质量浓度与时间对 Q235 钢腐蚀行为的影响。 结果 腐蚀产物元素主要为 O,S,Al,Fe。 在铝酸钠溶液中,基体的表面会覆盖一层 Al2O3 保护膜,可以阻碍溶液中的硫离子穿透到基体表面,对基体起到一定的保护作用。 因此腐蚀初期及低质量浓度下,腐蚀速率缓慢;但随着质量浓度的增加、腐蚀时间的延长,保护膜被破坏,S2-穿过保护膜与基体反应,生成硫化物加速了腐蚀速率;当 S2-质量浓度增加到 6 g/ L,腐蚀时间为 9 d 时,硫化物被氧化成具有较稳定结构的氧化物,腐蚀被抑制。 结论 在铝酸钠溶液中,S2-质量浓度及腐蚀时间对腐蚀有一定的促进作用,但当腐蚀时间及 S2-质量浓度达到一定值时,腐蚀速率呈现减小的趋势,腐蚀被抑制。 |
| 英文摘要: |
| Objective To study the corrosion behavior of Q235 steel in the S2--containing sodium aluminate solution. Methods The production conditions were simulated to prepare the mother liquor. Salt spray corrosion method together with SEM and EDS analysis technology, combined with the corrosion weight loss dynamics equation and polarization curve were used to study the effects of the Na2 S concentration and time on the corrosion behavior of Q235 steel. Results The elements of corrosion products were mainly O, S, Al and Fe. In sodium aluminate solution, the surface of the substrate was covered with a layer of Al2 O3 protective film, which could hinder the penetration of sulfur ions in the solution to the substrate surface, and play a role in the protection of the matrix. Therefore, in the early corrosion stage and at low concentrations, the corrosion rate was low, but with the increase of the concentration and the prolonged corrosion time, the protective membrane was damaged, S2- passed through the protective film and reacted with the substrate, generating sulphide which accelerated the corrosion rate. When the S2- mass concentration increased to 6 g / L and the corrosion time was 9 d, sulfide was oxidized to oxide with a relatively stable structure, the corrosion was inhibited. Conclusion In sodium aluminate solution, S2- concentration and corrosion time had a certain promoting effect of corrosion , but when the corrosion time and S2- concentration reached a certain value, the corrosion rate showed a decreasing trend, the corrosion was inhibited. |