邓宇,余圣甫,闫宁,行舒乐,黄林兵.V / Nb 对电弧喷涂马氏体不锈钢合金涂层组织和性能的影响[J].表面技术,2013,42(6):27-31.
DENG Yu,YU Sheng-fu,YAN Ning,XING Shu-le,HUANG Lin-bing.Effects of V / Nb on Microstructure and Properties of Arc Sprayed Martensitic Stainless Steel Alloy Coatings[J].Surface Technology,2013,42(6):27-31 |
| V / Nb 对电弧喷涂马氏体不锈钢合金涂层组织和性能的影响 |
| Effects of V / Nb on Microstructure and Properties of Arc Sprayed Martensitic Stainless Steel Alloy Coatings |
| 投稿时间：2013-06-27 修订日期：2013-07-27 |
| DOI： |
| 中文关键词: 马氏体不锈钢合金 V Nb 高速电弧喷涂 磨损性能 结合强度 |
| 英文关键词:martensitic stainless steel alloy V Nb high velocity arc spraying abrasive wear resistance adhesion strength |
| 基金项目:广东省科技计划项目(2012B010200037) |
|
|
| Author | Institution |
| DENG Yu | College of Mechanical and Electrical Engineering, Guangdong University of Petrochemical Technology, Maoming 525000,China;Guangdong Province Key Laboratory of Petrochemical Equipments, Maoming 525000,China |
| YU Sheng-fu | College of Material Science and Engineering, Huazhong University of Science and Technology, Wuhan 430074,China |
| YAN Ning | College of Material Science and Engineering, Huazhong University of Science and Technology, Wuhan 430074,China |
| XING Shu-le | College of Material Science and Engineering, Huazhong University of Science and Technology, Wuhan 430074,China |
| HUANG Lin-bing | College of Material Science and Engineering, Huazhong University of Science and Technology, Wuhan 430074,China |
|
| 摘要点击次数: |
| 全文下载次数: |
| 中文摘要: |
| 目的 研究添加 V 和 Nb 对电弧喷涂马氏体不锈钢合金层组织和性能的影响规律。 方法 研制不同 V 和 Nb 含量的新型马氏体不锈钢电弧喷涂药芯丝材,利用高速电弧喷涂设备在 Q235 低碳钢板表面制备耐磨合金涂层,并对合金涂层的组织结构和性能进行研究。 结果 所制备的合金涂层成形良好,孔隙率较低,结构致密;涂层显微硬度值达 523 HV0 . 1 ,与基材间的平均结合强度值达 35 . 48 MPa,V 和 Nb的添加提高了合金涂层的耐磨损性能。 结论 添加适量的 V 和 Nb 合金元素,可以促进碳化物硬质相颗粒的形成,提高马氏体不锈钢合金涂层的综合性能。 |
| 英文摘要: |
| Objective To study effects of V and Nb on microstructure and properties of arc sprayed martensitic stainless steel alloy. Methods New arc sprayed martensitic stainless steel flux-cored wires with different amount of V / Nb were developed, and the wear resistant alloy coatings were prepared on the surface of the Q235 low-carbon steel by HAVS using the wire. The microstructure and properties of the alloy coatings were detected and analyzed by using the equipment such as SEM, XRD, microhardness tester and wear tester. Results The coatings had good forming properties, less porosity, uniformity of microstructure and compact structure. The average value of adhesion strength was about 35 . 48 MPa. The average microhardness value was about 523 HV0 . 1 , which was higher than that of 4 Cr13 coatings, and the abrasive wear resistance was enhanced with the additional use of elements V and Nb. Conclusion V / Nb could improve the forming of carbide hard phase particles in the coatings and enhance the performance of the alloy coatings. |