王春雨,李磊,韩飞,赵洪运.表面镀铝对22MnB5 钢薄板焊接性的影响[J].表面技术,2012,(6):37-39,43.
WANG Chun-yu,LI Lei,HAN Fei,ZHAO Hong-yun.Effects of Surface Hot-dipping Al on Welding of 22MnB5 Sheet[J].Surface Technology,2012,(6):37-39,43 |
| 表面镀铝对22MnB5 钢薄板焊接性的影响 |
| Effects of Surface Hot-dipping Al on Welding of 22MnB5 Sheet |
| 投稿时间：2012-07-30 修订日期：2012-12-20 |
| DOI： |
| 中文关键词: 热浸铝 22MnB5 钢 钨极氩弧焊 热输入 |
| 英文关键词:hot dipping Al 22MnB5 GTAW heat input |
| 基金项目:山东省自然科学基金(ZR 2011 EMM013) |
| 作者 | 单位 |
| 王春雨 | 哈尔滨工业大学(威海) 材料科学与工程学院, 威海264209 |
| 李磊 | 哈尔滨工业大学(威海) 材料科学与工程学院, 威海264209 |
| 韩飞 | 哈尔滨工业大学(威海) 材料科学与工程学院, 威海264209 |
| 赵洪运 | 哈尔滨工业大学(威海) 材料科学与工程学院, 威海264209 |
|
| Author | Institution |
| WANG Chun-yu | School of Materials Science and Engineering, Harbin Institute of Technology at Weihai, Weihai 264209, China |
| LI Lei | School of Materials Science and Engineering, Harbin Institute of Technology at Weihai, Weihai 264209, China |
| HAN Fei | School of Materials Science and Engineering, Harbin Institute of Technology at Weihai, Weihai 264209, China |
| ZHAO Hong-yun | School of Materials Science and Engineering, Harbin Institute of Technology at Weihai, Weihai 264209, China |
|
| 摘要点击次数: |
| 全文下载次数: |
| 中文摘要: |
| 在22MnB5 钢板表面浸镀铝,采用钨极氩弧焊的方法焊接浸铝钢板和裸钢板,通过?旌阜烨慕鹣嘈蚊埠筒舛ɡ於狭亚慷?研究了焊接热输入和表面镀铝对焊缝组织和拉伸性能的影响。结果表明:焊缝热影响区中的不完全淬火区组织由马氏体、铁素体等组成,是接头中的软化区,力学性能最低,断裂在此发生;热输入较低会引起未熔合等成形缺陷,过大则会使焊缝组织变得粗大,适宜的热输入在3800 J/ cm 左右;浸铝层的存在对焊接参数(即热输入)的选择有影响,但不影响焊接力学性能。 |
| 英文摘要: |
| Hot dip Al 22MnB5 sheet and bare sample were welded by GTAW. Microstructure of weld metal and tensile strength were observed and tested, the effects of heat input and surface hot-dipping Al on the heat affected zone and tensile strength were investigated. The result shows that the incomplete quenching zone is composed of ferrite and martensite. The incomplete quenching zone is soft zone and the lowest tensile strength is shown in this zone. Low heat input may cause lack of fusion, or other molding defects; But high heat input would become coarser grain sizes. The optimized heat input of hot dipping aluminized 22MnB5 is at 3800 J/ cm. The preparation of welding has been affected with dipping Al coating and tensile strength of joints have not affected. |