殷秀银,柏立庆,吴玉萍.扩散处理后的FeCrNi涂层结合强度与断口特征研究[J].表面技术,2012,(5):64-69.
YIN Xiu-yin,BAI Li-qing,WU Yu-ping.Research on the Bonding Strength and Fracture Morphology of the Diffusion Treated FeCrNi Coating[J].Surface Technology,2012,(5):64-69 |
| 扩散处理后的FeCrNi涂层结合强度与断口特征研究 |
| Research on the Bonding Strength and Fracture Morphology of the Diffusion Treated FeCrNi Coating |
| 投稿时间：2012-05-16 修订日期：2012-10-20 |
| DOI： |
| 中文关键词: FeCrNi涂层 断口形貌 扩散处理 滑移带 结合强度 |
| 英文关键词:FeCrNi coating fracture morphology diffusion treatment slip band bonding strength |
| 基金项目: |
| 作者 | 单位 |
| 殷秀银 | 上海锐漫机械制造有限公司,上海200245 |
| 柏立庆 | 上海锐漫机械制造有限公司,上海200245 |
| 吴玉萍 | 河海大学力学与材料学院,南京210098 |
|
| Author | Institution |
| YIN Xiu-yin | Shanghai Realman Mechanical Manufacturing Co., Ltd, Shanghai 200245, China |
| BAI Li-qing | Shanghai Realman Mechanical Manufacturing Co., Ltd, Shanghai 200245, China |
| WU Yu-ping | College of Mechanics and Materials, Hohai University, Nanjing 210098, China |
|
| 摘要点击次数: |
| 全文下载次数: |
| 中文摘要: |
| 对无底层和有NiCrAl底层的FeCrNi涂层进行扩散处理,之后使涂层在机械作用力下断裂,通过观察断面的SEM 形貌,研究了涂层的断裂机制、涂层与基体间以及涂层内部颗粒间的结合状态,分析了扩散处理提高涂层结合强度的机理。涂层的断口基本上呈现出由暗色区域、白亮区域和未熔颗粒构成。暗色区域内断口面主要为层状剥离断裂;白亮区域内部含有滑移带和台阶面,断裂以脆性解理和塑性滑移混合方式进行。 |
| 英文摘要: |
| After the FeCrNi coatings(with or without NiCrAl adhesive coating)were fractured by the mechanical force, which had been diffusion treated in advance, then the fracture mechanism, the bonding states between coating and substrate and the bonding states inter particles of coating were seriously studied by observing the section SEM morphology on the fracture, and the effect mechanisms of diffusion treatment on improving the bonding strength of coating were also discussed. The coating fracture surface mainly consists of gray area and bright area, layer peeled off brittle rupture, the bonding strength of this way is very lower; Instead, the bright area turns on plenty of"slip-band" and "step-face", with the way mixed with brittle cleavage and plastic slip together. |