蒲滕,奚愚生,欧忠文,韩克,艾青林,李琪敏.深管零件内壁专用镀铬添加剂性能研究[J].表面技术,2012,(2):35-37，63.
PU Teng,XI Yu-sheng,OU Zhong-wen,HAN Ke,AI Qing-lin,LI Qi-min.Property Study on Chromium Plating Additives for Interior Layer of Tubular Parts[J].Surface Technology,2012,(2):35-37，63 |
| 深管零件内壁专用镀铬添加剂性能研究 |
| Property Study on Chromium Plating Additives for Interior Layer of Tubular Parts |
| 投稿时间：2011-11-29 修订日期：2012-04-20 |
| DOI： |
| 中文关键词: 深管内壁镀铬 添加剂 沉积速度 锥差 |
| 英文关键词:tubular parts internal chromium plating additives deposition rate taper |
| 基金项目:科技人员服务企业行动项目(2009GJF10031) |
| 作者 | 单位 |
| 蒲滕 | 后勤工程学院化学与材料工程系,重庆401311 |
| 奚愚生 | 中国兵器工业第五九研究所,重庆400039 |
| 欧忠文 | 后勤工程学院化学与材料工程系,重庆401311 |
| 韩克 | 后勤工程学院化学与材料工程系,重庆401311 |
| 艾青林 | 重庆建设工业集团,重庆400054 |
| 李琪敏 | 重庆建设工业集团,重庆400054 |
|
| Author | Institution |
| PU Teng | Department of Chemistry and Materials Engineering, Logistic Engineering University, Chongqing 401311, China; |
| XI Yu-sheng | No.59 Institute of China Ordnance Industry, Chongqing 400039,China; |
| OU Zhong-wen | Department of Chemistry and Materials Engineering, Logistic Engineering University, Chongqing 401311, China; |
| HAN Ke | Department of Chemistry and Materials Engineering, Logistic Engineering University, Chongqing 401311, China; |
| AI Qing-lin | .Chongqing Construction Group, Chongqing 400054, China; |
| LI Qi-min | Chongqing Construction Group, Chongqing 400054, China; |
|
| 摘要点击次数: |
| 全文下载次数: |
| 中文摘要: |
| 基于深管零件内壁镀铬的特殊性,采用未加添加剂及加入自制深管零件内壁专用镀铬添加剂和普通添加剂的标准镀液分别进行深管内壁镀铬,利用称量法测定镀铬层沉积速度,采用磁性测厚仪分析镀铬层锥差,对镀铬层的内应力、抗腐蚀性能、耐磨性能进行了测定,并对镀铬层进行了扫描电镜分析。结果表明:专用添加剂能提高深管内壁镀铬的速度,降低锥差,提高铬层性能。 |
| 英文摘要: |
| Based on the speciality of tubular parts interior chromium plating, three kinds of chromium electroplating bath were studied, they were standard bath, ordinary additive bath, self-made additive bath. Chromium coating plated by those bath were analyzed, measured deposition rate by weighing method, analyzed taper of chromium plating by magnetic film thickner, corrosion resistance and wear-resisting property of each chromium coating were tested, internal stress of each chromium coating were measured, characterization the chromium coating with SEM. The results show that the self-made additive is beneficial to increase deposition rate of chromiucoating and property, reduce taper. |