周靖,张宏,马瑞永,张箭,沈承金.润滑条件下WC-CoCr涂层的磨损行为[J].表面技术,2012,(2):26-29.
ZHOU Jing,ZHANG Hong,MA Rui-yong,ZHANG Jian,SHEN Cheng-jin.Tribological Behaviour of WC-CoCr Coatings under Lubrication Conditions[J].Surface Technology,2012,(2):26-29 |
| 润滑条件下WC-CoCr涂层的磨损行为 |
| Tribological Behaviour of WC-CoCr Coatings under Lubrication Conditions |
| 投稿时间：2011-12-27 修订日期：2012-04-20 |
| DOI： |
| 中文关键词: 超音速火焰喷涂 WC-CoCr 摩擦磨损 磨损机制 润滑 |
| 英文关键词:HVOF WC-CoCr friction and wear wear mechanism lubrication |
| 基金项目: |
| 作者 | 单位 |
| 周靖 | 中国矿业大学材料科学与工程学院,徐州221008 |
| 张宏 | 徐州工程集团挖掘机械有限公司,徐州221004 |
| 马瑞永 | 徐州工程集团挖掘机械有限公司,徐州221004 |
| 张箭 | 徐州工程集团挖掘机械有限公司,徐州221004 |
| 沈承金 | 中国矿业大学材料科学与工程学院,徐州221008 |
|
| Author | Institution |
| ZHOU Jing | School of Material Science and Engineering, China University of Mining & Technology, Xuzhou 221008, China |
| ZHANG Hong | XCMG Excavator Machinery Limited Company, Xuzhou 221004, China |
| MA Rui-yong | XCMG Excavator Machinery Limited Company, Xuzhou 221004, China |
| ZHANG Jian | XCMG Excavator Machinery Limited Company, Xuzhou 221004, China |
| SHEN Cheng-jin | School of Material Science and Engineering, China University of Mining & Technology, Xuzhou 221008, China |
|
| 摘要点击次数: |
| 全文下载次数: |
| 中文摘要: |
| 研究了在润滑条件下,WC-CoCr涂层与SiC摩擦副对磨时的摩擦和磨损性能,分析了加载载荷和润滑条件(干摩擦、润滑脂、金刚石研磨膏)对WC-CoCr涂层摩擦系数和磨损量的影响规律,对涂层的磨损机理进行了探讨。实验结果表明:脂润滑时,WC-CoCr涂层与SiC摩擦副对磨时的摩擦系数和磨损率降为最小,其中摩擦系数基本在0.1左右波动;金刚石研磨膏润滑时,磨损率高达1.52124×10-6g/m,为干摩擦条件下的2.68倍,抗磨减摩效果不理想;干摩擦时,涂层表面存在硬挤压痕,主要磨损机制为微切削并伴随着塑性变形,而在金刚石研磨膏润滑条件下,三体磨粒磨损起主导作用。 |
| 英文摘要: |
| The friction and wear properties of WC-CoCr coatings and SiC as counterparts under lubrication were analyzed. The effect of loads and dry conditions, diamond grinding paste conditions, oil conditions on the friction coefficient and wear rate were studied, and the wear mechanism was investigated. The results show that: under oil conditions, the friction coefficient and the wear rate of the coatings are both the lowest, and the friction coefficient is changed around 0.1; under diamond grinding lubrication, the friction coefficient is lower than dry conditions,the wear rate is 1.52124×10-6g/m, 2.68 times higher than dry conditions, the lubricity is bad; Extrusion marks are found on the surface of coatings under the dry conditions, and the wear mechanism is adhesion and slight cutting, while the three-body abrasion is the main under the diamond grinding pastes conditions. |