苏艳,朱玉琴,康凤.Ti8LC钛合金与主要结构材料的电偶腐蚀及防护研究[J].表面技术,2010,39(5):39-41,50.
SU Yan,ZHU Yu-qin,KANG Feng.The Study on Galvanic Corrosion and Surface Protection between Ti8LC Titanium Alloy and Central Structural Material[J].Surface Technology,2010,39(5):39-41,50
Ti8LC钛合金与主要结构材料的电偶腐蚀及防护研究
The Study on Galvanic Corrosion and Surface Protection between Ti8LC Titanium Alloy and Central Structural Material
投稿时间:2010-07-15  修订日期:2010-10-10
DOI:
中文关键词:  Ti8LC钛合金  铝合金  高强钢  电偶腐蚀  表面防护
英文关键词:Ti8LC titanium alloy  aluminum alloy  high strength steel  galvanic corrosion  surface protecting treatment
基金项目:
作者单位
苏艳 1.重庆大学化学化工学院,重庆400044;2.中国兵器工业第五九研究所,重庆400039 
朱玉琴 中国兵器工业第五九研究所,重庆400039 
康凤 中国兵器工业第五九研究所,重庆400039 
AuthorInstitution
SU Yan 1.College of Chemistry& Chemical Engineering, Chongqing University, Chongqing 400044, China;2.No.59 Institute of China Ordnance Industry, Chongqing 400039, China 
ZHU Yu-qin No.59 Institute of China Ordnance Industry, Chongqing 400039, China 
KANG Feng No.59 Institute of China Ordnance Industry, Chongqing 400039, China 
摘要点击次数:
全文下载次数:
中文摘要:
      通过测定表面防护处理前后,Ti8LC钛合金、7710铝合金、ZL59铝合金、30CrMnSiA高强钢的电极电位,以及Ti8LC钛合金与其余3种材料组成偶对后的电偶腐蚀电流-时间曲线,研究了表面防护处理前后3种偶对的电偶腐蚀行为,并评估了电偶腐蚀敏感性。研究结果表明:Ti8LC与7710铝合金、ZL59铝合金、30CrMnSiA钢偶接时,会产生严重的电偶腐蚀,必须进行表面防护处理才能使用;采用涂层前处理+有机涂层防护的方法,可有效阻止Ti8LC钛合金与铝合金和高强钢的电偶腐蚀。
英文摘要:
      Galvanic corrosion of Ti8LC titanium alloy coupled with 7710, ZL59 aluminum alloys and 30CrMnSiA high strength steel was studied through measurement of open circuit potential and galvanic current. Galvanic corrosion behavior of the three couples was studied before and after protecting treatment and their galvanic corrosion sensitivity was evaluated. The results show that when Ti8LC titanium alloy couples with 7710 aluminum alloy,ZL59 aluminum alloy, 30CrMnSiA high strength steel, there is serious galvanic corrosion, so the alloy must be suface protecting treated befor use; Surface treatment and organic coating can prevent the galvanic corrosion of titanium alloy coupled with aluminum alloys and high strength steel.
查看全文  查看/发表评论  下载PDF阅读器
关闭

关于我们 | 联系我们 | 投诉建议 | 隐私保护 | 用户协议

您是第24071016位访问者    渝ICP备15012534号-3

版权所有:《表面技术》编辑部 2014 surface-techj.com, All Rights Reserved

邮编:400039 电话:023-68792193传真:023-68792396 Email: bmjs@surface-techj.com

渝公网安备 50010702501715号