邵志松,赵晴,张淑娟.铝合金表面微弧氧化Cr2O3复合膜层的制备及表征[J].表面技术,2010,39(4):65-68.
SHAO Zhi-song,ZHAO Qing,ZHANG Shu-juan.Preparation and Characterization of MAO Film on Aluminium Surface with Cr2O3[J].Surface Technology,2010,39(4):65-68
铝合金表面微弧氧化Cr2O3复合膜层的制备及表征
Preparation and Characterization of MAO Film on Aluminium Surface with Cr2O3
投稿时间:2010-06-17  修订日期:2010-08-10
DOI:
中文关键词:  微弧氧化  复合膜层  三氧化二铬  复合量
英文关键词:MAO  composite film  chromium trioxide  composite amount
基金项目:
作者单位
邵志松 南昌航空大学,南昌330063 
赵晴 南昌航空大学,南昌330063 
张淑娟 江西科技师范学院,南昌330013 
AuthorInstitution
SHAO Zhi-song Nanchang Hangkong University, Nanchang 330063, China 
ZHAO Qing Nanchang Hangkong University, Nanchang 330063, China 
ZHANG Shu-juan Jiangxi Science&Technology Normal University, Nanchang 330013, China 
摘要点击次数:
全文下载次数:
中文摘要:
      在微弧氧化液中添加Cr2O3微粒对6063铝合金进行微弧氧化,研究了电解液中Cr2O3的浓度和各项工艺参数对复合膜层膜厚及表面形貌的影响,并用SEM,EDS等手段对复合膜层的微观形貌及组成进行了表征。结果表明:膜层厚度及Cr2O3的复合量均随着溶液中Cr2O3的含量、电流密度、微弧氧化时间的增加而增加,电解液的pH值对复合沉积量也有影响;复合膜层表面含有大量Cr2O3微粒,且Cr2O3微粒已沉积到了氧化膜内部。
英文摘要:
      The micro-arc oxidation(MAO)films were prepared on 6063 aluminum alloy in the electrolyte with Cr2O3particles, the effects of Cr2O3concentration in the electrolyte and the process parameters on the properties of the composite film were studied. The micro-morphology was investigated by the scanning electron microscopy(SEM), Energy dispersion spectrometer was used to analyze composition of the film. The results show that the Cr2O3concentrations in film and the film thickness are bothincreased with the increasement of Cr2O3concentrationsin solution,current density and MAO time; The Electrolyte pHinfluences composite amount; There are a large number of Cr2O3particles on the oxide film surface, and the Cr2O3particles are deposited to the oxide film internal.
查看全文  查看/发表评论  下载PDF阅读器
关闭

关于我们 | 联系我们 | 投诉建议 | 隐私保护 | 用户协议

您是第20721438位访问者    渝ICP备15012534号-3

版权所有:《表面技术》编辑部 2014 surface-techj.com, All Rights Reserved

邮编:400039 电话:023-68792193传真:023-68792396 Email: bmjs@surface-techj.com

渝公网安备 50010702501715号