李刚,侯俊英,刘丽,水东莉,唐海鹏,陈永君.激光熔覆Ni基非晶复合涂层组织结构及性能研究[J].表面技术,2010,39(4):15-17,24.
LI Gang,HOU Jun-ying,LIU Li,SHUI Dong-li,TANG Hai-peng,CHEN Yong-jun.Study on Microstructure and Properties of the Ni-based Amorphous Composite Coating Prepared by Laser Cladding[J].Surface Technology,2010,39(4):15-17,24
激光熔覆Ni基非晶复合涂层组织结构及性能研究
Study on Microstructure and Properties of the Ni-based Amorphous Composite Coating Prepared by Laser Cladding
  修订日期:2010-08-10
DOI:
中文关键词:  激光熔覆  45钢  组织  性能
英文关键词:laser cladding  45 steel  microstructure  properties
基金项目:辽宁省教育厅科技研究资助项目(2008297)
作者单位
李刚 辽宁工程技术大学,阜新123000 
侯俊英 辽宁工程技术大学,阜新123000 
刘丽 辽宁工程技术大学,阜新123000 
水东莉 辽宁工程技术大学,阜新123000 
唐海鹏 辽宁工程技术大学,阜新123000 
陈永君 辽宁工程技术大学,阜新123000 
AuthorInstitution
LI Gang Liaoning Technical University, Fuxin 123000, China 
HOU Jun-ying Liaoning Technical University, Fuxin 123000, China 
LIU Li Liaoning Technical University, Fuxin 123000, China 
SHUI Dong-li Liaoning Technical University, Fuxin 123000, China 
TANG Hai-peng Liaoning Technical University, Fuxin 123000, China 
CHEN Yong-jun Liaoning Technical University, Fuxin 123000, China 
摘要点击次数:
全文下载次数:
中文摘要:
      在45钢基体表面预涂覆Ni42Zr30Ta28合金粉末,采用DL-HL-T5000B型无氦横流CO2激光器进行激光熔覆制备非晶复合涂层。利用X射线衍射仪、金相显微镜对熔覆层进行微观组织分析,同时进行了硬度及摩擦性能测试。结果表明:熔覆层组织主要由金属间化合物(Fe7Ta3,Ni7Zr2,FeNi3,Ni3Ta等)、非晶相及纳米晶组成。当功率为3.3 kW时,熔覆层硬度达到最高,为2 954.3HK;磨损率最小,为0.571 mg/mm2。
英文摘要:
      Ni42Zr30Ta28alloy powder was pre-coated on 45 steel surface. Amorphous composite coating was prepared with DL-HL-T5000B-type cross-flow CO2laser helium-free. The microstructure was analyzed with XRD and metallurgical microscope analysis, meanwhile the hardness and friction properties of the layers were tested. The result shows that the coating is composed of intermetallic compounds, amorphous and nanocrystals, for example, Fe7Ta3, Ni7Zr2, FeNi3, Ni3Ta etc. The hardness of cladding layer reaches the maximum at the power of 3.3 kW, which is 2 954.3HK, and the wear rate is the lowest, which is 0.571 mg/mm2.
查看全文  查看/发表评论  下载PDF阅读器
关闭

关于我们 | 联系我们 | 投诉建议 | 隐私保护 | 用户协议

您是第20720962位访问者    渝ICP备15012534号-3

版权所有:《表面技术》编辑部 2014 surface-techj.com, All Rights Reserved

邮编:400039 电话:023-68792193传真:023-68792396 Email: bmjs@surface-techj.com

渝公网安备 50010702501715号