郭文才,谭俊,苏强,周亮.电流特性和纳米颗粒对电刷镀复合镀层耐腐蚀性能的影响[J].表面技术,2008,37(4):26-28.
GUO Wen-cai,TAN Jun,SU Qiang,ZHOU liang.Effect of Current Characteristic and Nano Powders on the Corrosion Resistance of Composite oatings by Brush-plating[J].Surface Technology,2008,37(4):26-28 |
| 电流特性和纳米颗粒对电刷镀复合镀层耐腐蚀性能的影响 |
| Effect of Current Characteristic and Nano Powders on the Corrosion Resistance of Composite oatings by Brush-plating |
| 投稿时间：2008-03-20 修订日期：2008-08-10 |
| DOI： |
| 中文关键词: 直流 脉冲 脉冲换向 电刷镀 纳米复合镀层 |
| 英文关键词:Direct current ( DC ) Pulse current ( PC ) Pulse-reverse current ( RC ) Electro brush-plating Nano composite coating |
| 基金项目:国家自然科学基金重点项目( 50235030)；装备再制造技术国防科技重点实验室基金项目( 514890201041S9102) |
| 作者 | 单位 |
| 郭文才 | 驻重庆北碚区军代室，重庆400700 |
| 谭俊 | 装备再制造技术国防科技重点实验室，北京100072 |
| 苏强 | 驻重庆北碚区军代室，重庆400700 |
| 周亮 | 驻长沙地区军代室，湖南长沙410014 |
|
| Author | Institution |
| GUO Wen-cai | Beibei Military Representive Office, Chongqing 400700, China |
| TAN Jun | National Key Laboratory for Remanufacturing, Beijing 100072, China |
| SU Qiang | Beibei Military Representive Office, Chongqing 400700, China |
| ZHOU liang | Changsha Military Representive Office, Changsha 410014, China |
|
| 摘要点击次数: |
| 全文下载次数: |
| 中文摘要: |
| 为获得性能优良的镀层，利用不同的电沉积方法（直流、脉冲电流及脉冲换向电流）制得了Ni、Ni/n,-Sio2和Ni/n,-Al2 03复合镀层，分别对其表面形貌(SEM)进行了观测和分析，测试了镀层的孔隙率，并通过海水浸泡方法检测其耐腐蚀性能。比较测试结果后发现：电流特性和纳米颗粒对电刷镀复合镀层的耐腐蚀性能均有影响，采用脉冲换向电流沉积得到的Ni/n-Si02复合镀层具有致密精细的表面形貌、较小的孔隙率和较好的耐腐蚀性能。 |
| 英文摘要: |
| For getting coatings with better corrosion resistance, the Ni/n,-Si02 and Ni/n,-Al203 coatings were preaped by different currents ( direct current, pulse current and pulse-reverse current) . Morphology, porosity and the corrosion resistance were tested respectively. The comparison of the results show that both current and nano powders can affect the corrosion resistance of composite coatings, the Ni/n-Si02 coating by pulse-reverse electro-plating has better advantages in the performance of morphology, porosity and corrosion resistance. |