| LIANG Cun-guang,LI Xin-mei,ZHANG Peng-fei.Erosion Wear Behavior of WC-12Co Coatings Prepared by APS[J],46(9):7-12 |
| Erosion Wear Behavior of WC-12Co Coatings Prepared by APS |
| Received:March 15, 2017 Revised:September 20, 2017 |
| View Full Text View/Add Comment Download reader |
| DOI：10.16490/j.cnki.issn.1001-3660.2017.09.002 |
| KeyWord:atmospheric plasma spraying WC-12Co composite coating erosion wear micro-hardness decarbonization cross-sectional images |
| Author | Institution |
| LIANG Cun-guang |
School of Mechanical Engineering, Xinjiang University, Urumqi , China |
| LI Xin-mei |
School of Mechanical Engineering, Xinjiang University, Urumqi , China |
| ZHANG Peng-fei |
School of Mechanical Engineering, Xinjiang University, Urumqi , China |
|
| Hits: |
| Download times: |
| Abstract: |
| To study the erosion wear resistance of WC-12Co composite coatings. in this paper,WC-12Co composite coatings was prepared on Q235 steel substrate by atmospheric plasma spraying (APS) method. The microstructure, phase composition and erosion wear be-havior of the obtained coatings were studied by using a variety of analytical techniques, such as XRD, SEM, EDS and self-made dry sand erosion wear tester. The mechanical properties of the coating were characterized by the Vivtorinox microhardness tester. showed that the coatings was mainly composed of WC, and a small amount of W2C, Co3W3C and Co6W6C phase. The coatings was about 300 m thick,the bonding coatings was about 50 m thick, and the cross-sectional microhardness was 1169HV0.05 at a load of 0.5 N. The maximum mass loss of the coating is 0.4788 mg/g at 60 degrees, and the minimum mass loss of the coating is about 0.3696 mg/g at 30 degrees. the wear loss firstly increase then decrease with the growth of the erosion angle, and amounted to the maximum value when the erosion angle was 60°. The coatings mainly subjected to plastic wear at the small angle (30°) while it subjected to brittle one at the large angle (90°). |