张世红,齐振伟,王梦迪,陈艳芬.柚子皮提取物对C38的缓蚀作用[J].表面技术,2014,43(1):51-54.
ZHANG Shi-hong,QI Zhen-wei,WANG Meng-di,CHEN Yan-fen.Corrosion Inhibition of C38 by Pomelo Peel Extract[J].Surface Technology,2014,43(1):51-54
柚子皮提取物对C38的缓蚀作用
Corrosion Inhibition of C38 by Pomelo Peel Extract
投稿时间:2013-11-04  修订日期:2014-01-16
DOI:
中文关键词:  柚子皮提取物  天然绿色缓蚀剂  KI  电化学测试
英文关键词:pomelo peel extract  natural green inhibitor  KI  electrochemical test
基金项目:
作者单位
张世红 西南石油大学 化学化工学院, 成都 610500 
齐振伟 西南石油大学 化学化工学院, 成都 610500 
王梦迪 西南石油大学 化学化工学院, 成都 610500 
陈艳芬 淮安自来水有限公司, 淮安 223001 
AuthorInstitution
ZHANG Shi-hong College of Chemistry and Chemical Engineering, Southwest Petroleum University, Chengdu 610500, China 
QI Zhen-wei College of Chemistry and Chemical Engineering, Southwest Petroleum University, Chengdu 610500, China 
WANG Meng-di College of Chemistry and Chemical Engineering, Southwest Petroleum University, Chengdu 610500, China 
CHEN Yan-fen Huai'an Tap Water Co. , Ltd, Huai'an 223001, China 
摘要点击次数:
全文下载次数:
中文摘要:
      目的 研究柚子皮提取物对 C38 钢在 1 mol / L HCl 中的缓蚀作用。 方法 通过索氏提取器从柚子皮中提取天然绿色缓蚀剂,进而与 0 . 01 mol / L KI 进行复配,采用失重法和电化学测试法分析柚子皮提取物的缓蚀作用机理。 结果 失重实验表明,柚子皮提取物对 C38 钢的缓蚀作用最高达 93% ,而与 0 . 01mol / L KI 复配使用后缓蚀效率最高达 98% 以上。 同时表明其在碳钢表面的吸附符合 Langmuir 吸附等温式;Tafel 极化曲线表明其能同时抑制碳钢腐蚀的阴、阳极过程;碳钢的阻抗值随着柚子皮提取物浓度的增加而增大。 结论 柚子皮提取物是很好的缓蚀剂,与卤素离子复配后效果更佳。
英文摘要:
      Objective To investigate the performance of pomelo peel extract in corrosion inhibition in 1 mol / L HCl. Methods A natural green corrosion inhibitor was extracted from pomelo peel using soxhlet extraction method, and the mechanism of corrosion inhibition of the extract was analyzed in a complex with 0. 01 mol / L KI. Weight-loss and Electrochemical tests were used. Results The result of weight-loss test showed that the corrosion inhibition of the extract to C38 steel was up to 93% , and it reached up to over 98% when used in a complex with 0. 01 mol / L KI. It was also shown that the adsorption of the inhibitor molecules on the surface of C38 steel obeyed Langrnuir isotherm. The Tafel polarization curves indicated that both anodic and cathodic corrosion processes were suppressed by the inhibitor. The EIS indicated that the charge transfer resistance increased with the increase of the inhibitor concentration. Conclusion Pomelo peel extract is a good corrosion inhibitor and the effect enhanced by the addition of halogen ions.
查看全文  查看/发表评论  下载PDF阅读器
关闭

关于我们 | 联系我们 | 投诉建议 | 隐私保护 | 用户协议

您是第13543706位访问者    渝ICP备15012534号-3

版权所有:《表面技术》编辑部 2014 surface-techj.com, All Rights Reserved

邮编:400039 电话:023-68792193传真:023-68792396 Email: wjqkbm@163.com

渝公网安备 50010702501715号