杨利,张桐,陈东旭,王亚男,周艳文,陈树江.化学气相沉积温度对AZ31镁合金表面制备DLC薄膜微观结构及机械性能的影响[J].表面技术,2020,49(5):317-324.
YANG Li,ZHANG Tong,CHEN Dong-xu,WANG Ya-nan,ZHOU Yan-wen,CHEN Shu-jiang.Effect of Temperature on Microstructures and Mechanical Properties of DLC Films Prepared on AZ31 Magnesium Alloy by Chemical Vapor Deposition[J].Surface Technology,2020,49(5):317-324 |
| 化学气相沉积温度对AZ31镁合金表面制备DLC薄膜微观结构及机械性能的影响 |
| Effect of Temperature on Microstructures and Mechanical Properties of DLC Films Prepared on AZ31 Magnesium Alloy by Chemical Vapor Deposition |
| 投稿时间：2019-06-02 修订日期：2020-05-20 |
| DOI：10.16490/j.cnki.issn.1001-3660.2020.05.038 |
| 中文关键词: 等离子体增强化学气相沉积 类金刚石薄膜 AZ31镁合金 沉积温度 机械性能 |
| 英文关键词:plasma enhanced chemical vapor deposition diamond-like-carbon film AZ31 magnesium alloy deposition temperature mechanical behavior |
| 基金项目:辽宁省自然科学基金（20180510001）；辽宁科技大学校人才计划（2018RC03）；辽宁省教育厅项目（SKLMEA-USTL(201709)，SKLMEA-USTLN (201909)）；辽宁科技大学创新团队项目（2017TD01） |
|
|
| Author | Institution |
| YANG Li | School of Materials and Metallurgy, University of Science and Technology Liaoning, Anshan 114051, China |
| ZHANG Tong | School of Materials and Metallurgy, University of Science and Technology Liaoning, Anshan 114051, China |
| CHEN Dong-xu | School of Materials and Metallurgy, University of Science and Technology Liaoning, Anshan 114051, China |
| WANG Ya-nan | School of Materials and Metallurgy, University of Science and Technology Liaoning, Anshan 114051, China |
| ZHOU Yan-wen | School of Materials and Metallurgy, University of Science and Technology Liaoning, Anshan 114051, China |
| CHEN Shu-jiang | School of Materials and Metallurgy, University of Science and Technology Liaoning, Anshan 114051, China |
|
| 摘要点击次数: |
| 全文下载次数: |
| 中文摘要: |
| 目的 提高镁合金表面硬度及耐磨性，给出最佳性能薄膜的制备温度。方法 采用化学气相沉积（PECVD）技术在AZ31镁合金表面制备了含氢DLC薄膜，研究了沉积温度对DLC薄膜厚度、表面形貌、硬度、杨氏模量、耐磨性能、膜基结合力以及sp3键含量的影响，并对相应的影响机制进行了讨论。结果 沉积温度对AZ31镁合金表面DLC膜的组织及性能有显著影响。温度较低时，碳粒子能量较低，无法注入薄膜亚表层，只能停留在表面以sp2杂化方式生长。随着温度的升高，碳粒子能量增加，更多的sp3杂化键形成。沉积温度为75 ℃时，薄膜中sp3杂化键含量最多，此时薄膜最厚约为7.67 μm，硬度最大可达5.95 GPa，杨氏模量值最高达到43.2 GPa，并且摩擦系数最低仅为0.03。随着温度进一步升高，碳粒子能量持续增加，轰击薄膜表面时会使碳-氢键断裂，造成氢的脱附，使薄膜中sp3杂化键减少，从而降低了薄膜的硬度及耐磨性等机械性能。结论 在本研究工作温度范围内，75 ℃为AZ31镁合金表面制备DLC薄膜的最佳温度。 |
| 英文摘要: |
| The work aims to enhance the surface hardness and wear resistance of magnesium alloy. Provide the optimal preparation temperature of excellent properties of the film. A hydrogen-containing DLC film was prepared on the surface of AZ31 magnesium alloy by plasma-enhanced chemical vapor deposition (PECVD) technology. The effects of deposition temperatures on the thickness, surface morphologies, hardness, Young’s modulus, wear resistance, bonding force and the contents of sp3 bond were studied. The corresponding mechanism of the influence of temperature was also discussed. The results show that the deposition temperatures have significant effect on the microstructures and properties of the DLC film on the surface of AZ31 magnesium alloy. At lower temperatures, the energy of carbon particles were lower. Therefore, the carbon particles cannot be injected into the subsurface of the film. They can only stay on the surface and growth by the form of sp2 hybrid. With the increase of temperature, the energy of carbon particles were increased and more sp3 hybrid bonds were formed. The hybrid forms of DLC film are mainly sp3 bonds at the deposition temperature is 75 ℃. At this temperature, the value of film thickness is about 7.67 μm, the value of film hardness is 5.95 GPa, the value of film Young's modulus is 43.2 GPa and the value of film friction coefficient is only 0.03. As the further increase of temperature, the energy of the carbon particles are increased continually. Therefore, the carbon-hydrogen bonds are broken under the bombardment of high energy carbon particles. The bombardment can result in the desorption of hydrogen, which can reduce the content of sp3 hybrid bond in the film. Therefore, the mechanical properties such as hardness and wear resistance are decreased. In this study, the optimum temperature for the preparation of DLC film on the surface of AZ31 magnesium alloy is 75 ℃. |