李冬伊,张盼盼,郭心瑜,赵晓伟,许英.胡萝卜茎叶提取物对碳钢在0.5 mol/L H2SO4溶液中的缓蚀作用[J].表面技术,2020,49(3):239-247.
LI Dong-yi,ZHANG Pan-pan,GUO Xin-yu,ZHAO Xiao-wei,XU Ying.Corrosion Inhibition Effect of Daucus Carota Stem and Leaf Extracts on Carbon Steel in 0.5 mol/L H2SO4 Solution[J].Surface Technology,2020,49(3):239-247
胡萝卜茎叶提取物对碳钢在0.5 mol/L H2SO4溶液中的缓蚀作用
Corrosion Inhibition Effect of Daucus Carota Stem and Leaf Extracts on Carbon Steel in 0.5 mol/L H2SO4 Solution
投稿时间:2019-05-12  修订日期:2020-03-20
DOI:10.16490/j.cnki.issn.1001-3660.2020.03.030
中文关键词:  胡萝卜茎叶  缓蚀剂  碳钢  硫酸  极化曲线  电化学阻抗谱  吸附等温模型
英文关键词:daucus carota stems and leaves  corrosion inhibitor  carbon steel  sulphuric acid  potentiodynamic curves  EIS  adsorption isotherm model
基金项目:河南省科技发展计划资助项目(162300410005);开封市科技发展计划项目(ZD17005)
作者单位
李冬伊 1.河南大学 化学化工学院,河南 开封 475004;2.郑州工业应用技术学院 药学与化学工程学院,郑州 451150 
张盼盼 1.河南大学 化学化工学院,河南 开封 475004 
郭心瑜 1.河南大学 化学化工学院,河南 开封 475004 
赵晓伟 1.河南大学 化学化工学院,河南 开封 475004 
许英 1.河南大学 化学化工学院,河南 开封 475004;2.郑州工业应用技术学院 药学与化学工程学院,郑州 451150 
AuthorInstitution
LI Dong-yi 1.School of Chemistry and Chemical Engineering, Henan University, Kaifeng 475004, China; 2.School of Pharmacy and Chemical Engineering, Zhengzhou University of Industrial Technology, Zhengzhou 451150, China 
ZHANG Pan-pan 1.School of Chemistry and Chemical Engineering, Henan University, Kaifeng 475004, China 
GUO Xin-yu 1.School of Chemistry and Chemical Engineering, Henan University, Kaifeng 475004, China 
ZHAO Xiao-wei 1.School of Chemistry and Chemical Engineering, Henan University, Kaifeng 475004, China 
XU Ying 1.School of Chemistry and Chemical Engineering, Henan University, Kaifeng 475004, China; 2.School of Pharmacy and Chemical Engineering, Zhengzhou University of Industrial Technology, Zhengzhou 451150, China 
摘要点击次数:
全文下载次数:
中文摘要:
      目的 研究胡萝卜茎叶提取物(DCSLE)在硫酸介质中对碳钢的腐蚀抑制作用及机理。方法 通过超声辅助的手段,用水浸提获得DCSLE,利用红外光谱(FTIR)对其含有的主要官能团进行表征。在25~40 ℃下,采用失重法、电化学极化和阻抗法(EIS)评价DCSLE在0.5 mol/L H2SO4溶液中对碳钢的缓蚀性能,并讨论了其缓蚀机理。结果 DCSLE对碳钢在0.5 mol/L H2SO4溶液中的腐蚀具有良好的抑制效果,其缓蚀效率随浓度的增加而增加,随温度的增加而先增加后降低(40 ℃<25 ℃<30 ℃<35 ℃),35 ℃下,质量浓度为0.6 g/L时,缓蚀效率为92.85%。电化学测试表明,DCSLE是混合型缓蚀剂,但主要是抑制阴极的反应。其缓蚀机理是:DCSLE以物理和化学混合吸附的方式吸附在碳钢表面,形成一层保护膜,从而阻止酸溶液的侵蚀,且吸附遵循Langmuir吸附等温模型。扫描电镜(SEM)观察到加入DCSLE后,碳钢的腐蚀得到了明显控制。结论 DCSLE可以有效抑制碳钢在0.5 mol/L H2SO4溶液介质中的腐蚀,是一种具有广泛应用前景的天然绿色缓蚀剂。
英文摘要:
      The paper aims to study the inhibitive action of DCSLE on carbon steel in sulfuric acid medium. DCSLE were obtained by soaking and ultrasonic method with water as solvent and its main functions were characterized by FTIR. The inhibition effect of DCSLE on carbon steel corrosion in 0.5 mol/L H2SO4 solution was studied by weight loss method, potentiodynamic curves and electrochemical impedance spectroscopic (EIS) at 25~40 ℃ and the corresponding corrosion mechanism was discussed. The results showed that DCSLE had a good inhibition effect on carbon steel in 0.5 mol/L H2SO4 solution. Its inhibition efficiency increased with increase of concentration, and decreased with the increase of (40 ℃< 25 ℃< 30 ℃< 35 ℃). The inhibition performance reached to 92.85% with 0.6 g/L at 35 ℃. The electrochemical test showed that DCSLE was a mixed inhibitor which mainly inhibited the cathode reaction. The inhibition mechanism of DCSLE was that DCSLE was adsorbed on the surface of carbon steel by a mixture of physical and chemical adsorptions, forming a protective film to prevent the corrosion of acid solution, and the adsorption followed the Langmuir adsorption isotherm model. SEM showed that the corrosion of carbon steel was obviously controlled by adding DCSLE. The DCSLE can effectively inhibit the corrosion of carbon steel in 0.5 mol/L H2SO4 solution. It is a natural green corrosion inhibitor with wide application prospects.
查看全文  查看/发表评论  下载PDF阅读器
关闭

关于我们 | 联系我们 | 投诉建议 | 隐私保护 | 用户协议

您是第19516218位访问者    渝ICP备15012534号-3

版权所有:《表面技术》编辑部 2014 surface-techj.com, All Rights Reserved

邮编:400039 电话:023-68792193传真:023-68792396 Email: bmjs@surface-techj.com

渝公网安备 50010702501715号