毛圣玫,许晓磊,于志伟.F51双相不锈钢离子渗氮层的组织与性能[J].表面技术,2020,49(2):185-191.
MAO Sheng-mei,XU Xiao-lei,YU Zhi-wei.Microstructure and Properties of Plasma Nitrided F51 Duplex Stainless Steel[J].Surface Technology,2020,49(2):185-191
F51双相不锈钢离子渗氮层的组织与性能
Microstructure and Properties of Plasma Nitrided F51 Duplex Stainless Steel
投稿时间:2019-05-05  修订日期:2020-02-20
DOI:10.16490/j.cnki.issn.1001-3660.2020.02.023
中文关键词:  离子渗氮  F51双相不锈钢  渗氮层  显微组织  硬度  耐磨性
英文关键词:plasma nitriding  F51 duplex stainless steel  nitrided layer  microstructure  hardness  wear resistance
基金项目:
作者单位
毛圣玫 大连海事大学,大连 116026 
许晓磊 大连海事大学,大连 116026 
于志伟 大连海事大学,大连 116026 
AuthorInstitution
MAO Sheng-mei Dalian Maritime University, Dalian 116026, China 
XU Xiao-lei Dalian Maritime University, Dalian 116026, China 
YU Zhi-wei Dalian Maritime University, Dalian 116026, China 
摘要点击次数:
全文下载次数:
中文摘要:
      目的 提高F51双相不锈钢的硬度以及耐磨性能。方法 将F51双相不锈钢进行低温(450 ℃)和高温(550 ℃)离子渗氮处理,利用光学显微镜(OM)、扫描电子显微镜(SEM)观察F51双相不锈钢渗氮层的微观组织,利用X射线衍射(XRD)方法对渗氮层沿深度方向相组成的变化进行分析,采用显微硬度计、摩擦磨损实验机分别对渗氮层的显微硬度及耐磨性能进行测试,采用激光扫描共聚焦显微镜(LSCM)对磨痕形貌进行观察。结果 F51双相不锈钢低温渗氮层主要由γN相组成,由表及里为γN→γN+aN (少量);高温渗氮层主要由CrN+aN相组成,由表及里为CrN+aN→aN+γN。高温渗氮层厚度约为低温渗氮层厚度的3倍。低温渗氮样品的平均表面硬度约为基体表面硬度的3.5倍;高温渗氮样品的平均表面硬度约为基体硬度的4倍。基体的摩擦系数约为0.71,低温和高温渗氮处理后样品的摩擦系数大大降低,分别为0.24和0.17。渗氮样品磨痕的宽度和深度较基体显著降低。结论 F51双相不锈钢低温渗氮层主要由gN相组成,高温渗氮层主要由CrN+aN相组成,两种温度渗氮后的样品硬度和耐磨性均得到显著提高。
英文摘要:
      The paper aims to improve the hardness and wear resistance of F51 duplex stainless steel. The F51 duplex stainless steel was nitrided at 450 ℃ and 550 ℃. The microstructure of the nitrided layer of F51 duplex stainless steel was observed by optical microscopy (OM) and scanning electron microscopy (SEM). The phase composition change of the nitrided layer in different depth was measured by X-ray diffraction (XRD). The microhardness and the wear resistance were evaluated by microhardness tester and friction wear tester respectively. The surface wear tracks were observed by laser scanning confocal microscope (LSCM). The low-temperature nitrided layer of F51 duplex stainless steel was mainly composed of phase γN and the phase distribution from the surface to the inner was γN→γN+aN (little). The high-temperature nitrided layer was mainly composed of phases CrN + aN, the phase distribution from surface to the inner was CrN+aN→aN+γN. The high-temperature nitrided layer was 3 times thicker than the low-temperature nitrided layer. The average surface hardness of the low-temperature nitrided sample was 3.5 times as high as the untreated sample; while the average surface hardness of the high-temperature nitrided sample was 4 times as high as the untreated sample. The friction coefficient of untreated sample was 0.71. While the friction coefficients of low-temperature and high-temperature nitrided layers were greatly reduced, which were 0.24 and 0.17, respectively. The width and the depth of surface wear tracks of the nitrided samples were reduced obviously compared with the untreated sample. The low-temperature nitrided layer of F51 duplex stainless steel mainly consists of phase gN, and the high-temperature nitrided layer mainly consists of phases CrN+aN. Both hardness and wear resistance of nitrided samples are effectively improved.
查看全文  查看/发表评论  下载PDF阅读器
关闭

关于我们 | 联系我们 | 投诉建议 | 隐私保护 | 用户协议

您是第20047607位访问者    渝ICP备15012534号-3

版权所有:《表面技术》编辑部 2014 surface-techj.com, All Rights Reserved

邮编:400039 电话:023-68792193传真:023-68792396 Email: bmjs@surface-techj.com

渝公网安备 50010702501715号