张东亚,孙喜洲,高峰,钟善军,段继豪.表面织构参数对液压马达滑靴副的摩擦学性能影响研究[J].表面技术,2019,48(4):230-236.
ZHANG Dong-ya,SUN Xi-zhou,GAO Feng,ZHONG Shan-jun,DUAN Ji-hao.Effect of Texture Parameters on Tribological Performance of Slipper Surface in Hydraulic Motor[J].Surface Technology,2019,48(4):230-236
表面织构参数对液压马达滑靴副的摩擦学性能影响研究
Effect of Texture Parameters on Tribological Performance of Slipper Surface in Hydraulic Motor
投稿时间:2018-09-27  修订日期:2019-04-20
DOI:10.16490/j.cnki.issn.1001-3660.2019.04.033
中文关键词:  液压马达滑靴副  正交试验  表面织构  承载力  摩擦系数
英文关键词:hydraulic motor slipper pair  orthogonal test  surface texture  bearing capacity  friction coefficient
基金项目:国家自然科学基金(51605381);陕西省自然科学基金(2017JQ5101);中国博士后科学基金项目(2017M613171);陕西省教育厅自然科学专项(17JK0544)
作者单位
张东亚 1.西安理工大学 机械与精密仪器工程学院,西安 710048 
孙喜洲 1.西安理工大学 机械与精密仪器工程学院,西安 710048 
高峰 1.西安理工大学 机械与精密仪器工程学院,西安 710048 
钟善军 2.宁波中意液压马达有限公司,浙江 宁波 315200 
段继豪 1.西安理工大学 机械与精密仪器工程学院,西安 710048 
AuthorInstitution
ZHANG Dong-ya 1.School of Mechanical and Precision Instrument Engineering, Xi’an University of Technology, Xi’an 710048, China 
SUN Xi-zhou 1.School of Mechanical and Precision Instrument Engineering, Xi’an University of Technology, Xi’an 710048, China 
GAO Feng 1.School of Mechanical and Precision Instrument Engineering, Xi’an University of Technology, Xi’an 710048, China 
ZHONG Shan-jun 2.Ningbo Zhongyi Hydraulic Motor Co., Ltd, Ningbo 315200, China 
DUAN Ji-hao 1.School of Mechanical and Precision Instrument Engineering, Xi’an University of Technology, Xi’an 710048, China 
摘要点击次数:
全文下载次数:
中文摘要:
      目的 通过表面织构改善液压马达连杆滑靴副的摩擦学性能。方法 首先,基于Reynolds方程研究表面织构参数(直径d、面密度sp、深度hp)对滑靴副的无量纲压力(Pav)的影响规律。其次,设计正交试验研究表面织构参数对摩擦系数的影响,分析表面织构的润滑机理。结果 Pav随着d的增加而增大;随着sp的增大,先增加后缓慢减小,当sp=10%时,Pav达到最大值。此外,随着hp的增大,Pav先增加后快速减小,在hp=2 μm时达到最大值。摩擦实验结果表明,合适的织构参数能有效降低摩擦系数,7#织构表面(d=700 μm,sp=10%,hp=5 μm)的摩擦系数最小为0.034,比无织构表面的降低66%。正交极差分析表明,各因素对摩擦系数影响的主次顺序为:直径>面密度>深度。摩擦系数随着直径的增大而减小,随着面密度的增大而增大,随着深度的增大而减小。结论 经过优选的表面织构参数有利于形成动压润滑,从而降低摩擦系数和磨损。
英文摘要:
      The work aims to improve the tribological performance of the hydraulic motor slipper pair by surface texture. Firstly, the effect of surface texture parameters (diameter d, surface density sp, depth hp) on the dimensionless bearing capacity (Pav) of textured connecting rod surface was investigated based on Reynolds equation. Secondly, the friction coefficients of surface texture with different parameters were studied by orthogonal experiments, and the corresponding lubrication mechanism was analyzed. Pav increased linearly with the increase of d, while Pav first increased and then decreased with the increase of sp, and the maximum Pav was obtained at sp of 10%. As the hp increased, Pav first increased and then decreased and reached the maximum at hp of 2 μm. The friction coefficient of the textured surface with suitable parameters was effectively reduced. The 7# surface (d=700 μm, sp=10%, hp=5 μm) had a minimum friction coefficient of 0.034, which was 66% lower than that of the non-textured surface. Range analysis showed that the influence order of factors on the friction coefficient was: diameter>area density>depth. The friction coefficient decreased with increase of diameter and depth, but increased with the increase of area density. The surface texture parameters through selection are beneficial to formation of dynamic pressure lubrication to reduce friction coefficient.
查看全文  查看/发表评论  下载PDF阅读器
关闭

关于我们 | 联系我们 | 投诉建议 | 隐私保护 | 用户协议

您是第19512995位访问者    渝ICP备15012534号-3

版权所有:《表面技术》编辑部 2014 surface-techj.com, All Rights Reserved

邮编:400039 电话:023-68792193传真:023-68792396 Email: bmjs@surface-techj.com

渝公网安备 50010702501715号