孙敏,吴国龙,王晔,张群莉,姚建华,Volodymyr S. Kovalenko.316L表面激光熔覆复合微弧氧化制备陶瓷涂层[J].表面技术,2019,48(2):24-32.
SUN Min,WU Guo-long,WANG Ye,ZHANG Qun-li,YAO Jian-hua,Volodymyr S. Kovalenko.Ceramic Coating Prepared by Laser Cladding and Composite Micro-arc Oxidation on 316L Surface[J].Surface Technology,2019,48(2):24-32 |
| 316L表面激光熔覆复合微弧氧化制备陶瓷涂层 |
| Ceramic Coating Prepared by Laser Cladding and Composite Micro-arc Oxidation on 316L Surface |
| 投稿时间：2018-10-23 修订日期：2019-02-20 |
| DOI：10.16490/j.cnki.issn.1001-3660.2019.02.004 |
| 中文关键词: 316L 激光熔覆 微弧氧化 生物活性 耐蚀性 |
| 英文关键词:316L laser cladding micro-arc oxidation bioactivity corrosion resistance |
| 基金项目:国家自然科学基金（51605441）；浙江省自然科学基金青年基金（LQ16E010004）；高等学校学科创新引智计划资助（110000213920168001） |
|
|
| Author | Institution |
| SUN Min | 1.Institute of Laser Advanced Manufacturing, Zhejiang University of Technology, Hangzhou 310014, China; 2.Zhejiang Provincial Collaboration Innovation Center of High-end Laser Manufacturing Equipment, Hangzhou 310014, China |
| WU Guo-long | 1.Institute of Laser Advanced Manufacturing, Zhejiang University of Technology, Hangzhou 310014, China; 2.Zhejiang Provincial Collaboration Innovation Center of High-end Laser Manufacturing Equipment, Hangzhou 310014, China |
| WANG Ye | 1.Institute of Laser Advanced Manufacturing, Zhejiang University of Technology, Hangzhou 310014, China; 2.Zhejiang Provincial Collaboration Innovation Center of High-end Laser Manufacturing Equipment, Hangzhou 310014, China |
| ZHANG Qun-li | 1.Institute of Laser Advanced Manufacturing, Zhejiang University of Technology, Hangzhou 310014, China; 2.Zhejiang Provincial Collaboration Innovation Center of High-end Laser Manufacturing Equipment, Hangzhou 310014, China |
| YAO Jian-hua | 1.Institute of Laser Advanced Manufacturing, Zhejiang University of Technology, Hangzhou 310014, China; 2.Zhejiang Provincial Collaboration Innovation Center of High-end Laser Manufacturing Equipment, Hangzhou 310014, China |
| Volodymyr S. Kovalenko | 1.Institute of Laser Advanced Manufacturing, Zhejiang University of Technology, Hangzhou 310014, China;3.Laser Technology Research Institute, National Technical University of Ukraine, Kiev 03056, Ukraine |
|
| 摘要点击次数: |
| 全文下载次数: |
| 中文摘要: |
| 目的 提高316L不锈钢表面的耐蚀性和生物活性。方法 首先采用激光熔覆技术在316L不锈钢表面制备钛层，然后对钛层表面进行微弧氧化处理，从而在316L不锈钢表面制备出含有Ca、P元素的多孔状陶瓷涂层。利用扫描电子显微镜（Scanning Electron Microscope，SEM）、能谱仪（Energy Dispersive Spectrometer，EDS）、X射线衍射仪（X-Ray Diffraction，XRD）分析了钛层厚度对陶瓷涂层的表面显微形貌、元素含量及物相组成的影响。利用电化学实验、浸泡实验分别测试了涂层在1.5倍SBF溶液中的耐蚀性能和生物活性。结果 通过激光熔覆复合微弧氧化能够在316L不锈钢表面制备出多孔状陶瓷涂层。随着钛层厚度的增加，微弧氧化原位生成的陶瓷涂层致密度、厚度也增加。当钛层厚度达到0.4 mm时，微弧氧化后得到的陶瓷涂层完整致密，厚度达到20 μm。涂层主要由锐钛矿相TiO2、金红石相TiO2组成。极化曲线分析可知，腐蚀电位Ecorr为-0.162 V，腐蚀电流密度降至5.11×10-7 A/cm2。陶瓷涂层在1.5倍SBF中浸泡3天后表面即有羟基磷灰石沉积。结论 通过激光熔覆复合微弧氧化在316L不锈钢表面制备的陶瓷涂层在模拟体液环境下具有较好的耐蚀性能，同时也具备良好的生物活性。 |
| 英文摘要: |
| The work aims to improve the corrosion resistance and bioactivity of 316L stainless steel surface. The titanium coating was prepared on 316L by laser cladding, and then the micro-arc oxidation was carried out on the surface of the titanium layer. Therefore, porous ceramic coating containing Ca and P was prepared on the surface of 316L. The influence of the thickness of titanium layer on the surface morphology, element content and phase composition of ceramic coating was analyzed by SEM (Scanning Electron Microscope), EDS (Energy Dispersive Spectrometer) and XRD (X-Ray Diffraction). The corrosion resistance and bioactivity of the coating in 1.5× SBF solution were tested by electrochemical tests and immersion tests. Porous ceramic coating was prepared on 316L stainless steel by laser cladding and composite micro arc oxidation. The density and thickness of ceramic coating in situ formed by micro-arc oxidation increased with increase of the thickness of titanium layer. When the thickness of titanium layer reached 0.4 mm, the ceramic coating prepared by micro-arc oxidation was dense and the thickness of the dense coating reached 20 μm. The coating mainly consisted of anatase phase and rutile phase. From the polarization curve, the corrosion potential Ecorr was -0.162 V and the corrosion current density decreased to 5.11×10-7 A/cm2. After immersion in 1.5 times of SBF for 3 days, hydroxyapatite was observed on the surface of the ceramic coating. The ceramic coating prepared by laser cladding combined with micro-arc oxidation on 316L surface has excellent corrosion resistance in simulated body fluid, and can effectively improve the bioactivity of 316L stainless steel. |