孟天旭,郭麒,席雯,丁文强,于盛旺,林乃明,刘小萍.刻蚀对高碳马氏体不锈钢表面等离子渗铬层结合强度的影响[J].表面技术,2019,48(1):276-284.
MENG Tian-xu,GUO Qi,XI Wen,DING Wen-qiang,YU Sheng-wang,LIN Nai-ming,LIU Xiao-ping.Effect of Etching on Bonding of Plasma Chromizing Layer on High Carbon Martensitic Stainless Steel[J].Surface Technology,2019,48(1):276-284 |
| 刻蚀对高碳马氏体不锈钢表面等离子渗铬层结合强度的影响 |
| Effect of Etching on Bonding of Plasma Chromizing Layer on High Carbon Martensitic Stainless Steel |
| 投稿时间：2018-04-03 修订日期：2019-01-20 |
| DOI：10.16490/j.cnki.issn.1001-3660.2019.01.036 |
| 中文关键词: 8Cr17不锈钢 等离子体刻蚀 渗铬 结合强度 |
| 英文关键词:8Cr17 stainless steel plasma etching chromizing bonding strength |
| 基金项目:国家自然科学基金（51474154, 51501125, 51601124） |
|
|
| Author | Institution |
| MENG Tian-xu | Research Institute of Surface Engineering, School of Materials Science and Engineering, Taiyuan University of Technology, Taiyuan 030024, China |
| GUO Qi | Research Institute of Surface Engineering, School of Materials Science and Engineering, Taiyuan University of Technology, Taiyuan 030024, China |
| XI Wen | Research Institute of Surface Engineering, School of Materials Science and Engineering, Taiyuan University of Technology, Taiyuan 030024, China |
| DING Wen-qiang | Research Institute of Surface Engineering, School of Materials Science and Engineering, Taiyuan University of Technology, Taiyuan 030024, China |
| YU Sheng-wang | Research Institute of Surface Engineering, School of Materials Science and Engineering, Taiyuan University of Technology, Taiyuan 030024, China |
| LIN Nai-ming | Research Institute of Surface Engineering, School of Materials Science and Engineering, Taiyuan University of Technology, Taiyuan 030024, China |
| LIU Xiao-ping | Research Institute of Surface Engineering, School of Materials Science and Engineering, Taiyuan University of Technology, Taiyuan 030024, China |
|
| 摘要点击次数: |
| 全文下载次数: |
| 中文摘要: |
| 目的 研究等离子体刻蚀工艺对高碳马氏体不锈钢表面渗铬层组织和结合强度的影响。方法 首先利用微波等离子体化学气相沉积方法对8Cr17马氏体不锈钢表面进行四种不同工艺参数的刻蚀处理，然后利用双层辉光等离子体表面渗铬技术在刻蚀处理后的8Cr17不锈钢表面制备铬合金层。用扫描电子显微镜、激光共聚焦、辉光放电光谱仪和X射线衍射仪分别表征刻蚀表面形貌和渗铬层组织，用划痕仪测试渗铬层与基体的结合强度。结果 氢和氢+氩等离子体刻蚀后，8Cr17不锈钢基体表面粗糙度增加，且含碳量减少。渗铬层由表面富Cr层、CrxCy扩散层、基体组成，其物相主要包括Cr、Cr23C6、Cr7C3。表面经氢气刻蚀1 h和2 h后，形成的渗铬层厚度分别为7、7.5 μm，氢气+氩气刻蚀1 h和2 h后，渗铬层厚度分别为8.1、9 μm，其中氢气+氩气刻蚀1 h的基材表面渗铬层较致密，与基体结合牢固。结论 等离子体刻蚀预处理可通过改变8Cr17钢表面的组织形貌，降低表面含碳量，增加扩散层厚度，提高渗层与基体的结合强度。 |
| 英文摘要: |
| The work aims to study the effect of plasma etching process on the structure and bonding strength of chromizing layer on the surface of 8Cr17 high carbon martensitic stainless steel. 8Cr17 steel was firstly etched with four different process pa-rameters by microwave plasma chemical vapor deposition method, and then the double glow plasma surface alloying was applied to prepare chromizing alloy layer on the etched 8Cr17 surface. Scanning electron microscopy, laser scanning confocal microscopy, glow discharge optical emission spectrometer and X-ray diffraction were used to characterize the morphology of etched surface and microstructure of chromizing layer. The bond strength between chromizing layer and substrate was measured by a scratch tester. The surface roughness increased, but the surface carbon was consumed after hydrogen and hydrogen + argon etching. The chromizing layer with Cr, Cr23C6 and Cr7C3 was composed of surface Cr rich layer/CrxCy diffusion layer/substrate. The thickness of the chromizing layer formed on the pretreated surface after hydrogen etching for 1 h and 2 h was 7.5 μm and 7.5 μm, and hy-drogen + argon etching for 1 h and 2 h was 8.1 μm and 9 μm, respectively, and the chromizing layer after hydrogen + argon etching for 1 h was dense and had a strong adherence to substrate. The etching process obviously results in an increase of the diffusion thickness as well as bonding strength between chromizing alloy layer and substrate. |