李定玉,王如转,李卫国,郑恒伟,王小荣.基于临界失效能密度判据的热障涂层热震损伤行为研究[J].表面技术,2019,48(1):56-61.
LI Ding-yu,WANG Ru-zhuan,LI Wei-guo,ZHENG Heng-wei,WANG Xiao-rong.Thermal Shock Damage Behaviour of Thermal Barrier Coatings Based on the Failure Energy Density Criteria[J].Surface Technology,2019,48(1):56-61 |
| 基于临界失效能密度判据的热障涂层热震损伤行为研究 |
| Thermal Shock Damage Behaviour of Thermal Barrier Coatings Based on the Failure Energy Density Criteria |
| 投稿时间：2018-09-20 修订日期：2019-01-20 |
| DOI：10.16490/j.cnki.issn.1001-3660.2019.01.008 |
| 中文关键词: 热障涂层 失效能密度 热震 有限元 损伤 |
| 英文关键词:thermal barrier coating failure energy density thermal shock finite element method damage |
| 基金项目:国家自然科学基金项目（11602043，11602044，11602042）；重庆市基础科学与前沿技术研究项目（cstc2017jcyjAX0240）；重庆市教育委员会科学技术研究项目（KJ1713323） |
|
|
| Author | Institution |
| LI Ding-yu | 1. Chongqing University of Science and Technology, Chongqing 401331, China |
| WANG Ru-zhuan | 1. Chongqing University of Science and Technology, Chongqing 401331, China |
| LI Wei-guo | 2.Chongqing University, Chongqing 400030, China |
| ZHENG Heng-wei | 1. Chongqing University of Science and Technology, Chongqing 401331, China |
| WANG Xiao-rong | 1. Chongqing University of Science and Technology, Chongqing 401331, China |
|
| 摘要点击次数: |
| 全文下载次数: |
| 中文摘要: |
| 目的 探索热障涂层系统（TBCs）在热震过程中的损伤行为。方法 基于材料能量储存极限，推导了适用于平面复杂应力情形的温度相关性临界失效能密度判据，进而利用该临界失效能密度判据与ABAQUS有限元软件相结合，研究了热生长氧化层（TGO）凸起的热障涂层系统在冷却热震过程中的损伤行为。结果 对于TGO层凸起的热障涂层系统，计算了冷却热震过程中陶瓷层（TC）和TGO层的失效能密度分布云图，并根据最大失效能分布情况分析了TBCs在热震过程中各层材料的可能破坏位置，所得结果与实验吻合较好。在对TBCs的冷却热震损伤行为模拟计算中发现，当TC层的强度比较低时，热震会使TC层上表面产生往内部扩展的垂直裂纹；当TC层强度达到某一定值时，首先发生热震破坏的位置由TC层上表面变成了TGO层与粘结层（BC）的界面处，即TBCs的各层破坏顺序发生了变化。结论 使用临界失效能密度准则来判断热障涂层在冷却热震过程中的损伤行为，比单纯使用某一方向应力更为准确，并能准确判断损伤起始位置和演化情况，从而更全面地反映热障涂层在热震过程中的损伤破坏行为。 |
| 英文摘要: |
| The work aims to investigate the damage behavior of thermal barrier coating system (TBCs) during the thermal shock. The temperature-dependent failure energy density criteria was deduced based on the energy storage limitation of material for plane complex stress condition. With the criteria and ABAQUS finite element software, thermal shock damage behavior of raised TBCs in the thermally grown oxide (TGO) was studied. The distribution of failure energy density in top-coat (TC) and TGO during cooling thermal shock was calculated for the raised TBCs in TGO and the damaged location of each layer in TBCs during the thermal shock was analyzed according to the maximum failure energy distribution. The obtained results agreed well with the experiment results. Furthermore, the simulation of thermal shock damage evolution behavior for TBCs showed that vertical cracks growth towards inside layer could be produced in TC under thermal shock when the strength of TC was relative lower. However, the firstly damaged location could change to the interface between TGO and BC (bond-coat) from the upper surface of TC when the strength of TC reached a certain value. The damage order of each layer in TBCs changed. Therefore, the failure energy density criteria is more accurate to characterize the thermal shock damage behavior of TBCs than the stress of one direction and can also determine the exact location of damage initiation and the evolution of damage, thus revealing the thermal shock failure for TBCs comprehensively. |
| 查看全文 查看/发表评论 下载PDF阅读器 |