郑兴睿,刘成,于晓华,张雁南,刘建雄.无铬复合钝化膜的微观组织结构及耐腐蚀性能[J].表面技术,2018,47(8):197-203.
ZHENG Xing-rui,LIU Cheng,YU Xiao-hua,ZHANG Yan-nan,LIU Jian-xiong.Microstructure and Corrosion Resistance of Chromium-free Composite Passive Film[J].Surface Technology,2018,47(8):197-203 |
| 无铬复合钝化膜的微观组织结构及耐腐蚀性能 |
| Microstructure and Corrosion Resistance of Chromium-free Composite Passive Film |
| 投稿时间：2018-01-24 修订日期：2018-08-20 |
| DOI：10.16490/j.cnki.issn.1001-3660.2018.08.027 |
| 中文关键词: 镀锌板 无铬钝化 复合钝化膜 微观组织结构 耐蚀性能 |
| 英文关键词:galvanized sheet chromium-free passivation composite passive film microstructure corrosion resistance |
| 基金项目:国家 863 计划项目（2009AA03Z529）；国家自然科学基金（51601081） |
|
|
| Author | Institution |
| ZHENG Xing-rui | City School, Kunming University of Science and Technology, Kunming 650093, China |
| LIU Cheng | National Engineering Research Center of Solid Waste Resource, Kunming University of Science and Technology, Kunming 650093, China |
| YU Xiao-hua | National Engineering Research Center of Solid Waste Resource, Kunming University of Science and Technology, Kunming 650093, China |
| ZHANG Yan-nan | National Engineering Research Center of Solid Waste Resource, Kunming University of Science and Technology, Kunming 650093, China |
| LIU Jian-xiong | National Engineering Research Center of Solid Waste Resource, Kunming University of Science and Technology, Kunming 650093, China |
|
| 摘要点击次数: |
| 全文下载次数: |
| 中文摘要: |
| 目的 解决热镀锌钢板表面六价铬钝化工艺所产生的环境污染问题。方法 以钼酸铵、纳米硅溶胶、单宁酸、硅烷偶联剂 KH151 和 KH792 为主要原料配制新型环保的无铬复合钝化液，在镀锌板表面制备钝化膜。采用扫描电子显微镜（SEM）、能谱仪（EDS）和 X 射线光电子能谱仪（XPS）分析无铬复合钝化膜表面的微观形貌、元素组成和化学成分，用电化学工作站测试 Mo 元素对镀锌板耐蚀性的影响，使用中性盐雾实验研究不同皮模量时膜层的耐蚀性。结果 无铬复合钝化膜中的 Mo 元素可以抑制微裂纹的产生和发展，阻挡腐蚀性介质向金属基体扩散，提高复合硅烷膜的电阻。复合钝化膜的电化学交流阻抗比硅烷钝化膜提高了 1.6 倍，与六价铬钝化膜接近，可以有效抑制腐蚀电化学反应的发生，降低反应速度，提高膜层的耐蚀性。皮膜量为 892 mg/m2时，膜层的腐蚀面积为 0，耐蚀性达到六价铬钝化膜水平；皮膜量为 1252 mg/m2 时，耐蚀性能优异。结论 制备的无铬复合钝化膜结合了硅烷钝化膜和钼酸盐钝化膜两方面的优点，提高了膜层的致密性和结合性，膜层耐腐蚀性接近/达到了六价铬钝化的效果。 |
| 英文摘要: |
| The work aims to solve the problem of environmental pollution caused by hexavalent chromium passivation process on the surface of hot galvanized steel sheet. A kind of new and environment-friendly chromium-free composite passive solution was prepared, which was mainly made from ammonium molybdate, nano silica sol, tannic acid, silane coupling agent KH151 and KH792. Microscopic morphology, elemental composition and chemical composition of the chromium-free composite passive film were analyzed by SEM, EDS and XPS. The effects of Mo on corrosion resistance of galvanized sheet were tested by electrochemical workstation, and corrosion resistance of the film at different weight was studied by performing neutral salt spray test. Mo element in the chromium-free composite passive film could inhibit generation and development of microcracks, prevent corrosive mediums from spreading toward metallic substrate, and improve resistance of the composite silane film. Electrochemical impedance of the composite passivation film was 1.6 times higher than that of the silane passive film (close to that of Cr6+ passive film), which could inhibit corrosion electrochemical reaction, reduce reaction speed and strengthen corrosion resistance of the film. In addition, corrosion resistance was comparable with that of Cr6+ film as the film reached 892 mg/m2 and corrosion area was 0; and the corrosion resistance was excellent as the film reached 1252 mg/m2. The chromium-free composite passive film combines the advantages of both silane passivation film and molybdate passivation film, compactness and combinability are better, and corrosion resistance of the film is close to/achieves the effect of hexavalent chromium passivation. |