周昌欢,林晨,张娟娟,王清春,杜圣恩.镍基钎料对45#钢激光熔覆镍基WC合金熔覆层缺陷的影响[J].表面技术,2018,47(3):91-95.
ZHOU Chang-huan,LIN Chen,ZHANG Juan-juan,WANG Qing-chun,DU Sheng-en.Effect of Ni-based Solder on Defects of Laser Cladding WC Alloy Layers on 45# Steel[J].Surface Technology,2018,47(3):91-95
镍基钎料对45#钢激光熔覆镍基WC合金熔覆层缺陷的影响
Effect of Ni-based Solder on Defects of Laser Cladding WC Alloy Layers on 45# Steel
投稿时间:2017-10-08  修订日期:2018-03-20
DOI:10.16490/j.cnki.issn.1001-3660.2018.03.015
中文关键词:  激光熔覆  表面工程  膏状镍基钎料  缺陷  摩擦磨损
英文关键词:laser cladding  surface engineering  pasty Ni-based solder  defect  friction and wear
基金项目:
作者单位
周昌欢 青岛理工大学 机械工程学院,山东 青岛 266520 
林晨 青岛理工大学 机械工程学院,山东 青岛 266520 
张娟娟 青岛理工大学 机械工程学院,山东 青岛 266520 
王清春 青岛理工大学 机械工程学院,山东 青岛 266520 
杜圣恩 青岛理工大学 机械工程学院,山东 青岛 266520 
AuthorInstitution
ZHOU Chang-huan School of Mechanical Engineering, Qingdao Technological University, Qingdao 266520, China 
LIN Chen School of Mechanical Engineering, Qingdao Technological University, Qingdao 266520, China 
ZHANG Juan-juan School of Mechanical Engineering, Qingdao Technological University, Qingdao 266520, China 
WANG Qing-chun School of Mechanical Engineering, Qingdao Technological University, Qingdao 266520, China 
DU Sheng-en School of Mechanical Engineering, Qingdao Technological University, Qingdao 266520, China 
摘要点击次数:
全文下载次数:
中文摘要:
      目的 改善Ni60A+WC合金粉末激光熔覆中裂纹和气孔等缺陷性能。方法 在Ni60A+WC合金粉末中添加膏状镍基钎料(BNi-1a)改善激光熔覆层的裂纹和气孔缺陷。使用Rofin FL020光纤激光器,在1 kW功率、扫描速度为4 mm/s、光斑直径约为2 mm的条件下,对经过烘干的预涂覆合金熔覆层进行激光加工处理。通过显微硬度测试评价熔覆层的硬度,通过扫描电子显微镜和X射线衍射仪对熔覆层形貌、相组织进行分析,并通过UMT和表面形貌仪对熔覆层的摩擦系数和耐磨性进行评估。结果 在Ni60A+WC合金粉末中添加膏状镍基钎料(BNi-1a),优化了Cr和C合金相的组成,使熔覆层的裂纹和气孔等缺陷明显减低。添加膏状镍基钎料的熔覆层的摩擦系数约为0.45,熔覆层的摩擦系数大约降低了18%。同时熔覆层的耐磨性也有所提高,未添加膏状镍基钎料的熔覆层磨痕横截面积约为0.70103 mm2,而添加膏状镍基钎料的熔覆层横截面积约为0.50103 mm。结论 镍基钎料(BNi-1a)的加入可以有效减少熔覆层的裂纹和气孔等缺陷,同时提高熔覆层的耐磨性,但是使熔覆层的硬度有一定的降低。
英文摘要:
      The work aims to reduce defects such as cracks and pores in laser cladding of Ni60A +WC alloy powder. Pasty Ni-based solder (BNi-1a) was added into Ni60A+WC alloy powder to reduce defects such as cracks and pores in laser cladding layers. Provided with power of 1 kW, scanning speed of 4 mm/s and spot diameter of nearly 2 mm, Rofin FL020 fiber laser was used for laser processing of baked pre-coated alloy cladding layers. Microhardness test was conducted to evaluate hardness of the cladding layers, morphology and phase structure of the layers were studied with SEM and XRD. Friction coefficient and wear resistance of the layers were evaluated with UMT and surface morphology tester. Composition of Cr and C alloy phase was optimized, and defects such as cracks and pores were reduced by as pasty Ni-based solder (BNi-1a) was added into Ni60A+WC alloy powder. For the cladding layer with pasty Ni-based solder, friction coefficient was nearly 0.45, friction coefficient of the cladding layer decreased by nearly 18%, wear resistance was also greatly increased, and cross-sectional area was nearly 0.50103 mm. For the cladding layer without pasty Ni-based solder, cross-sectional area of the grinding crack was nearly 0.70103 mm2. The addition of Ni-based solder (BNi-1a) can effectively reduce defects including cracks and pores, and improve wear resistance and reduce hardness, but it may reduce hardness of cladding layers.
查看全文  查看/发表评论  下载PDF阅读器
关闭

关于我们 | 联系我们 | 投诉建议 | 隐私保护 | 用户协议

您是第19507968位访问者    渝ICP备15012534号-3

版权所有:《表面技术》编辑部 2014 surface-techj.com, All Rights Reserved

邮编:400039 电话:023-68792193传真:023-68792396 Email: bmjs@surface-techj.com

渝公网安备 50010702501715号