翟永杰,刘秀波,乔世杰,徐江宁,耿荣华,彭勇.热处理对TA2合金表面激光熔覆Ti2SC/TiS涂层组织和力学性能的影响[J].表面技术,2017,46(6):207-214.
ZHAI Yong-jie,LIU Xiu-bo,QIAO Shi-jie,XU Jiang-ning,GENG Rong-hua,PENG Yong.Influence of Heat Treatment on Microstructure and Mechanical Properties of Laser Cladding Ti2SC/TiS Coating on TA2 Alloy[J].Surface Technology,2017,46(6):207-214 |
| 热处理对TA2合金表面激光熔覆Ti2SC/TiS涂层组织和力学性能的影响 |
| Influence of Heat Treatment on Microstructure and Mechanical Properties of Laser Cladding Ti2SC/TiS Coating on TA2 Alloy |
| 投稿时间：2017-01-20 修订日期：2017-06-20 |
| DOI：10.16490/j.cnki.issn.1001-3660.2017.06.033 |
| 中文关键词: 激光熔覆 TA2合金 热处理 钛基 自润滑 耐磨减摩 |
| 英文关键词:laser cladding TA2 alloy heat treatment Ti-based self-lubrication wear resistance and antifriction |
| 基金项目:国家自然科学基金委员会-中国民航局民航联合研究基金（U1533101）；武汉理工大学材料复合新技术国家重点实验室开放基金（2017-KF-05）；苏州市科技计划项目（SYG201635） |
|
|
| Author | Institution |
| ZHAI Yong-jie | School of Mechanical and Electric Engineering, Soochow University, Suzhou 215006, China |
| LIU Xiu-bo | 1.School of Mechanical and Electric Engineering, Soochow University, Suzhou 215006, China;2.State Key Laboratory of Tribology, Tsinghua University, Beijing 100084, China |
| QIAO Shi-jie | School of Mechanical and Electric Engineering, Soochow University, Suzhou 215006, China |
| XU Jiang-ning | School of Mechanical and Electric Engineering, Soochow University, Suzhou 215006, China |
| GENG Rong-hua | School of Mechanical and Electric Engineering, Soochow University, Suzhou 215006, China |
| PENG Yong | School of Mechanical and Electric Engineering, Soochow University, Suzhou 215006, China |
|
| 摘要点击次数: |
| 全文下载次数: |
| 中文摘要: |
| 目的 对激光熔覆自润滑耐磨涂层进行热处理，获得具有较好摩擦学性能的复合涂层。方法 采用激光熔覆技术在TA2合金表面熔覆40%Ti-25.2%TiC-34.8%WS2复合粉末制备自润滑耐磨复合涂层。将涂层置于500 ℃真空中分别保温1、2 h，采用扫描电镜（SEM）、X射线衍射仪（XRD）、能谱仪（EDS）、显微硬度计、摩擦磨损试验机以及原子力显微镜（AFM）系统地分析了热处理前后涂层的物相、组织、显微硬度及摩擦学性能。结果 未经过热处理和经过热处理涂层的主要物相均为α-Ti、(Ti,W)C1－x、TiC、Ti2SC和TiS。相比未经热处理涂层的显微硬度（1049.8 HV0.5），经过热处理1 h和2 h涂层的显微硬度（1143.3 HV0.5和1162.7 HV0.5）有所上升。热处理1 h和2 h涂层的摩擦系数和磨损率分别为0.29和6.66×10−5 mm3/(N•m)以及0.29和5.65×10−5 mm3/(N•m)，比未热处理涂层（0.32和18.92×10−5 mm3/(N•m)）的耐磨减摩性能有所提升。经过热处理1 h和2 h涂层的磨损机理均主要表现为磨粒磨损，未经热处理涂层的磨损机理主要为塑性变形和粘着磨损。结论 相比未经热处理的涂层，经过热处理1 h和2 h的涂层显微硬度有所升高，摩擦学性能得到提升，但在两种热处理时间条件下，涂层显微硬度和摩擦学性能变化较小。 |
| 英文摘要: |
| The work aims to obtain composite coatings of better tribological properties by performing heat treatment to laser cladding self-lubricating wear-resistant coatings. The composite coatings were fabricated by cladding 40% Ti-25.2% TiC-34.8%WS2 composite powder on TA2 alloy by taking advantage of laser cladding technology.The coatings were kept at 500 ℃ in vacuum for 1 h and 2 h, respectively, and then phases, microstructure, microhardness and tribological property of the coatings subject to heat treatment or not were analyzed with scanning electron microscope (SEM), X-ray diffractometer (XRD), energy dispersive system (EDS), microhardness tester, friction wear testing machine and atomic force microscope (AFM) systematically. Main phases of the coatings subject to heat treatment or not were α-Ti, (Ti,W)C1－x, TiC, Ti2SC and TiS. Microhardness of the coatings subject to 1 h and 2 h heat treatment (1143.3HV0.5 and 1162.7HV0.5) has increased compared with that of coatings not subject to heat treatment (1049.8HV0.5). Coefficient of friction and wear rate of the coatings subject to 1 h and 2 h heat treatment were 0.29 and 6.66×10−5 mm3/(N•m), 0.29 and 5.65×10−5 mm3/(N•m), respectively. Compared with the coating not subject to heat treatment (0.32 and 18.92×10−5 mm3/(N•m)), those coatings subject to heat treatment exhibited better wear resistance and antifriction property. Wear mechanism of the coatings subject to 1 h and 2 h heat treatment was mainly presented as abrasive wear, while that of coatings not subject to heat treatment was mainly plastic deformation and adhesive wear. Compared with the coating not subject to heat treatment, microhardness and tribological properties of the coatings subject to 1 h and 2 h heat treatment have improved, but those of the coatings change slightly in different time of heat treatment. |