绢云母和硅烷偶联剂KH550对聚氨酯/Al-Sm2O3复合涂层耐盐水性能的影响
Effects of Sericite and Silane Coupling Agent KH550 on Saline Water Resistance of Polyurethane/Al-Sm2O3 Composite Coatings
投稿时间:2016-12-19  修订日期:2017-05-20
DOI:10.16490/j.cnki.issn.1001-3660.2017.05.016
中文关键词:  复合涂层  绢云母  硅烷偶联剂  红外发射率  近红外反射率  力学性能
英文关键词:composite coatings  sericite  silane coupling agent  infrared emissivity  near-infrared reflectivity  mechanical properties
基金项目:安徽省高校自然科学研究重点项目(KJ2016A535);国家级大学生创新训练计划项目(201610377021);安徽省大学生创新训练计划项目(201610377055);滁州学院大学生创新训练计划项目(2016CXXL063)
作者单位
赵运林 滁州学院,安徽 滁州 239000 
张伟钢 滁州学院,安徽 滁州 239000 
AuthorInstitution
ZHAO Yun-lin Chuzhou University, Chuzhou 239000, China 
ZHANG Wei-gang Chuzhou University, Chuzhou 239000, China 
摘要点击次数:
全文下载次数:
中文摘要:
      目的 提高聚氨酯(PU)/Al-Sm2O3复合涂层的耐盐水性能。方法 以绢云母和硅烷偶联剂KH550改性PU/Al-Sm2O3复合涂层,系统研究改性前后涂层的微结构、红外发射率、近红外反射率及力学性能经盐水腐蚀后的变化规律,并对其成因进行分析探讨。结果 经绢云母和KH550改性后的涂层与改性前的涂层相比,其微结构在腐蚀前后几乎保持不变,经盐水腐蚀相同时间时,改性涂层具有更低的1.06 µm近红外反射率,更优异的力学性能。改性涂层经盐水腐蚀10 d后,其硬度、附着力和耐冲击强度仍可保持在3H、1级和50 kgcm。结论 绢云母和KH550改性可明显提高PU/Al-Sm2O3复合涂层的近红外低反射性能及力学性能对盐水腐蚀的稳定性。
英文摘要:
      The work aims to improve saline water resistance of polyurethane(PU)/Al-Sm2O3 composite coatings. PU/Al- Sm2O3 composite coatings were modified with sericite and silane coupling agent KH550, and varying patterns of microstructure, infrared emissivity, near-infrared reflectivity and mechanical properties of the coatings before and after modification were systematically investigated, then the causes were analyzed and discussed. Compared with the unmodified coatings, microstructure of the modified sericite and KH550 coatings was almost unchanged after corrosion, and the modified coatings had lower near-infrared reflectivity of 1.06 μm and better mechanical properties under the same corrosion conditions of saline water. Hardness, adhesion strength and impact strength of the modified coatings were maintained at 3H, grade 1 and 50 kgcm 10 days after saline water corrosion. Sericite and KH550 modification can improve the stability of low near-infrared reflection property and mechanical properties of PU/Al-Sm2O3 composite coatings to saline water corrosion.
查看全文  查看/发表评论  下载PDF阅读器
关闭

关于我们 | 联系我们 | 投诉建议 | 隐私保护 | 用户协议

您是第19515739位访问者    渝ICP备15012534号-3

版权所有:《表面技术》编辑部 2014 surface-techj.com, All Rights Reserved

邮编:400039 电话:023-68792193传真:023-68792396 Email: bmjs@surface-techj.com

渝公网安备 50010702501715号