刘光明,周街胜,王义元,刘志雷,黄健航,张正华,李四维.改性水滑石的制备及对环氧富锌漆性能的影响[J].表面技术,2017,46(3):223-228.
LIU Guang-ming,ZHOU Jie-sheng,WANG Yi-yuan,LIU Zhi-lei,HUANG Jian-hang,ZHANG Zheng-hua,LI Si-wei.Preparation of Modified Hydrotalcite and Its Effects on Performance of Epoxy Zinc-rich Paint[J].Surface Technology,2017,46(3):223-228 |
| 改性水滑石的制备及对环氧富锌漆性能的影响 |
| Preparation of Modified Hydrotalcite and Its Effects on Performance of Epoxy Zinc-rich Paint |
| 投稿时间：2016-09-27 修订日期：2017-03-20 |
| DOI：10.16490/j.cnki.issn.1001-3660.2017.03.034 |
| 中文关键词: KH560 环氧富锌漆 水滑石 改性 |
| 英文关键词:KH560 epoxy zinc-rich paint hydrotalcite modification |
| 基金项目:国家自然科学基金（51161022）；江西省教育厅项目（DB201301133，DB201301050） |
|
|
| Author | Institution |
| LIU Guang-ming | School of Materials Science and Engineering, Nanchang Hangkong University, Nanchang 330063, China |
| ZHOU Jie-sheng | School of Materials Science and Engineering, Nanchang Hangkong University, Nanchang 330063, China |
| WANG Yi-yuan | Shanghai Aerospace System Engineering Institute, Shanghai 201109, China |
| LIU Zhi-lei | School of Materials Science and Engineering, Nanchang Hangkong University, Nanchang 330063, China |
| HUANG Jian-hang | School of Materials Science and Engineering, Nanchang Hangkong University, Nanchang 330063, China |
| ZHANG Zheng-hua | SPIC Jiangxi Electric Power Co., Ltd, Jingdezhen Power Plant, Jingdezheng 333000, China |
| LI Si-wei | School of Science, Xian Jiaotong University, Xian 710049, China |
|
| 摘要点击次数: |
| 全文下载次数: |
| 中文摘要: |
| 目的 改善有机涂层和无机缓蚀剂相容性差的问题，实现缓蚀剂的可控释放，提高有机涂层的防护性能。方法 用共沉淀方法将缓蚀剂钼酸根离子插入镁铝水滑石中，并用硅烷偶联剂KH560对其表面接枝改性来提高填料在富锌涂层中的分散性。结果 XRD、FTIR光谱分析结果表明，水滑石的层间距离增大，钼酸根成功装载进水滑石层中，在水滑石表面成功接枝硅烷偶联剂KH560。结论 通过将该填料添加到环氧富锌漆中，发现涂层的附着力、柔韧性均没有发生明显的下降，表明填料在环氧富锌涂层中分散均匀，对涂层的力学性能影响较小。结合电化学阻抗谱技术对比研究添加填料与未添加填料的涂层浸泡在NaCl溶液中的腐蚀行为，表明了该填料的添加可以提高富锌漆的耐腐蚀性能。 |
| 英文摘要: |
| The work aims to improve the poor compatibility between organic coating and inorganic corrosion inhibitor, and realize the controlled release of corrosion inhibitor with the aim of improving protective property of organic coating. Magnesium aluminum hydrotalcite loaded with molybdate was synthesized by co-precipitation method. And the as-prepared hydrotalcite was modified by silane coupling agent KH560 to improve dispersion of pigments. The XRD and FTIR spectral analysis showed that the interlayer distance of hydrotalcite has been magnified, indicating that the molybdate has been inserted into the layers of hydrotalcite successfully, and silane coupling agent KH560 has been grafted to surface of as-prepared hydrotalcite. As KH560 modified filler was incorporated into epoxy zinc-rich paint, the adhesion and flexibility of coating show no obvious degradation, indicating that the filler disperse uniformly in the coating, fillers had smaller effect on mechanical properties of the coating. Furthermore, from the electrochemical impedance spectroscopy (EIS) we can conclude that the corrosion resistance of zinc-rich paint can be enhanced by adding the filler by studying corrosion behaviors of coatings with filler and without filler in NaCl solution. |