王军,刘莹,胡静茹.浸渍式提拉法制备TiO2薄膜的微观结构和润湿性[J].表面技术,2017,46(2):58-62.
WANG Jun,LIU Ying,HU Jing-ru.Microstructure and Wettability of TiO2 Thin Films Prepared by Dip Coating Method[J].Surface Technology,2017,46(2):58-62
浸渍式提拉法制备TiO2薄膜的微观结构和润湿性
Microstructure and Wettability of TiO2 Thin Films Prepared by Dip Coating Method
投稿时间:2016-08-18  修订日期:2017-02-20
DOI:10.16490/j.cnki.issn.1001-3660.2017.02.009
中文关键词:  溶胶-凝胶  TiO2薄膜  工艺参数  微观结构  光学性质  润湿性
英文关键词:TiO2 thin film  process parameter  microstructure  optical properties  wettability
基金项目:国家自然科学基金资助项目(51165031)
作者单位
王军 1.南昌大学 机电工程学院,南昌 330031;2.江西科技师范大学 江西省材料表面工程重点实验室,南昌 330031 
刘莹 南昌大学 机电工程学院,南昌 330031 
胡静茹 南昌大学 机电工程学院,南昌 330031 
AuthorInstitution
WANG Jun 1.School of Mechanical and Electrical Engineering, Nanchang University, Nanchang 330031, China; 2.Jiangxi Key Laboratory of Surface Engineering, Jiangxi Science and Technology Normal University, Nanchang 330031, China 
LIU Ying School of Mechanical and Electrical Engineering, Nanchang University, Nanchang 330031, China 
HU Jing-ru School of Mechanical and Electrical Engineering, Nanchang University, Nanchang 330031, China 
摘要点击次数:
全文下载次数:
中文摘要:
      目的 研究工艺参数与TiO2薄膜的微观结构、光学性质及润湿性的关系。方法 以钛酸四丁酯为原料,乙醇为溶剂,采用溶胶-凝胶浸渍式提拉法,改变工艺参数(提拉次数、提拉速度),在玻璃衬底上制备了TiO2薄膜,并通过光学表面形貌仪、紫外可见分光光度计及接触角测试仪分析了不同参数下制备的TiO2薄膜的微观结构、光学性质和润湿性。结果 提拉次数和提拉速度都会影响薄膜的微观结构,提拉2次,提拉速度在3~7 cm/min之间制备的TiO2薄膜表面平整、致密。在提拉方向上,存在厚度梯度,厚度梯度为1 nm/μm。透射光谱显示TiO2薄膜在可见光区透明,吸收边与提拉工艺有关,提拉速度为7 cm/min,提拉2次制备的TiO2薄膜,禁带宽度为3.57 eV,此时,接触角为14.8°。结论 提拉速度、提拉次数影响TiO2薄膜的微观结构、光学性质和润湿性。通过提拉工艺参数的调整,可以制备均匀致密、具有亲水性的半导体TiO2薄膜。
英文摘要:
      The work aims to investigate the relationship between process parameters and microstructure, optical properties, or wettability of TiO2 thin films. With tetrabutyl titanate as raw materials and ethanol as solvent, the TiO2 thin films were prepared on glass substrates with different process parameters (withdrawal times and withdrawal speed) by virtue of sol-gel dip coating method. The microstructure, optical properties and wettability of TiO2 thin films prepared with different process parameters were analyzed by optical surface microscopy, ultraviolet and visible spectrophotometer and contact angle tester. Microstructure of TiO2 thin films was influenced by withdrawal times and withdrawal speed. Uniform and dense films were produced provided with withdrawal times of 2 times and withdrawal speed of 3 to 7 cm/min. Thickness gradient (1 nm/μm) was present in the withdrawal direction. Transmitted spectrum showed that the TiO2 thin films were transparent in visible region. The absorption edge related to the withdrawal process. The forbidden band width of TiO2 film prepared at withdrawal speed of 7 cm/min and withdrawal times of 2 times was 3.57 eV while contact angle was 14.8°. The microstructure, optical properties and wettability of TiO2 thin films are influenced by withdrawal speed and withdrawal times. Uniform, dense and hydrophilic semiconductor TiO2 thin can be fabricated by adjusting the withdrawal process parameters.
查看全文  查看/发表评论  下载PDF阅读器
关闭

关于我们 | 联系我们 | 投诉建议 | 隐私保护 | 用户协议

您是第19496720位访问者    渝ICP备15012534号-3

版权所有:《表面技术》编辑部 2014 surface-techj.com, All Rights Reserved

邮编:400039 电话:023-68792193传真:023-68792396 Email: bmjs@surface-techj.com

渝公网安备 50010702501715号