朱培珂,闫伟,李令东,段保平,沈雪峰,王芹.油管钢在模拟超临界CO2中耐蚀特性的研究[J].表面技术,2016,45(12):167-173.
ZHU Pei-ke,YAN Wei,LI Ling-dong,DUAN Bao-ping,SHEN Xue-feng,WANG Qin.Corrosion Resistance of Tubing Steels in Simulated Supercritical Carbon Dioxide[J].Surface Technology,2016,45(12):167-173
油管钢在模拟超临界CO2中耐蚀特性的研究
Corrosion Resistance of Tubing Steels in Simulated Supercritical Carbon Dioxide
投稿时间:2016-06-30  修订日期:2016-12-20
DOI:10.16490/j.cnki.issn.1001-3660.2016.12.027
中文关键词:  CO2腐蚀  超临界  油管钢  点蚀  钝化
英文关键词:carbon dioxide corrosion  supercritical  tubing  pitting  passivate
基金项目:风险探井钻井随钻分析与后期评价研究
作者单位
朱培珂 中国石油勘探开发研究院,北京 100083 
闫伟 中国石油大学(北京)油气资源与探测国家重点实验室,北京 102249 
李令东 中国石油勘探开发研究院,北京 100083 
段保平 中国石油勘探开发研究院,北京 100083 
沈雪峰 中国石油技术开发公司,北京 100009 
王芹 中国石油勘探开发研究院,北京 100083 
AuthorInstitution
ZHU Pei-ke PetroChina Research Institute of Petroleum Exploration & Development, Beijing 100083, China 
YAN Wei State Key Laboratory of Petroleum Resource and Prospecting, China University of Petroleum, Beijing 102249, China 
LI Ling-dong PetroChina Research Institute of Petroleum Exploration & Development, Beijing 100083, China 
DUAN Bao-ping PetroChina Research Institute of Petroleum Exploration & Development, Beijing 100083, China 
SHEN Xue-feng China Petroleum Technology and Development Corporation, Beijing 100009, China 
WANG Qin PetroChina Research Institute of Petroleum Exploration & Development, Beijing 100083, China 
摘要点击次数:
全文下载次数:
中文摘要:
      目的 研究普通碳钢P110、3Cr、普通马氏体不锈钢13Cr和超级马氏体不锈钢HP2-13Cr钢在某油井超临界CO2环境中的耐蚀特性。方法 模拟该高温高压高含CO2且含Cl–油井的腐蚀环境,采用高温高压反应釜对上述四种油管钢进行挂片实验,借助高精度天平、扫描电子显微镜(SEM)、能量色散X射线能谱(EDS)从平均腐蚀速率、清理腐蚀产物后试样的表观特征、腐蚀产物的表面形貌和化学成分及腐蚀机制方面分析其抗均匀腐蚀与抗点蚀特性。结果 在CO2分压达12 MPa,110 ℃,Cl–质量浓度为16 542 mg/L的典型环境,P110,3Cr油管钢的平均腐蚀速率分别为5.625,2.992 mm/a;13Cr为0.155 mm/a,有点蚀发生,HP2-13Cr则为0.003 mm/a,且为均匀腐蚀,HP2-13Cr能满足模拟腐蚀环境的使用要求。结论 在上述超临界CO2环境,碳钢P110与3Cr在基体表面不存在Cr的富集,耐蚀性差;马氏体不锈钢13Cr和超级马氏体不锈钢HP2-13Cr因基体表面能生成致密的钝化膜,则表现出相对优良的耐蚀性,但两者的合金元素Ni,Mo含量不同,造成了对两者抗均匀腐蚀与抗点蚀性能的显著差异。
英文摘要:
      To research the corrosion resistance of normal carbon steel P110, 3Cr, martensitic stainless steel 13Cr and super-martensitic stainless steel HP2-13Cr in simulated supercritical CO2 environment. Methods The corrosive environment of high temperature/ high pressure/CO2 enriched and Cl– contained oil well was simulated. The above four kinds of steels were tested by blade-hanging with a high temperature and high pressure reactor. Their characteristics of anti-general corrosion and corrosive pitting were analysed in the aspects of average corrosion rate, surface characteristics of samples after clearing the corrosion products, surface morphology, composition of corrosion products and corrosion mechanism using high class electric balance, scanning electron microscopy (SEM) and energy dispersive spectroscopy (EDS). Results In the environment at 110 ℃ and containing 12 MPa partial pressure of CO2 and 16 542 mg/L Cl–, the average corrosion rate of P110 and 3Cr were 5.625 mm/a and 2.992 mm/a respectively. The corrosion rate of 13Cr was 0.155 mm/a and pitting corrosion occurred on its surface, the corrosion rate of HP2-13Cr was 0.003 mm/a and general corrosion occurred. HP2-13Cr met the using requirement in the corrosive environment. Conclusion In the above supercritical CO2 environment, the corrosion resistance of carbon steel P110 and 3Cr is low because no tight corrosion films containing rich Cr covered on their metal. The corrosion resistance of martensitic stainless steel 13Cr and super-martensitic stainless steel HP2-13Cr are better than the two former due to dense passivation film on the surface. However, the content difference of Ni and Mo contribute to significant difference in their resistance to general corrosion and corrosive pitting.
查看全文  查看/发表评论  下载PDF阅读器
关闭

关于我们 | 联系我们 | 投诉建议 | 隐私保护 | 用户协议

您是第19513003位访问者    渝ICP备15012534号-3

版权所有:《表面技术》编辑部 2014 surface-techj.com, All Rights Reserved

邮编:400039 电话:023-68792193传真:023-68792396 Email: bmjs@surface-techj.com

渝公网安备 50010702501715号