陈文,陶永元,管春平,胡小安.电化学法研究芭蕉叶提取物在盐酸中对碳钢的缓蚀作用[J].表面技术,2016,45(1):124-130,160.
CHEN Wen,TAO Yong-yuan,GUAN Chun-ping,HU Xiao-an.Electrochemical Investigation of Extracts of Musa Basjoo Leaves as Corrosion Inhibitor for Carbon Steel in Hydrochloric Acid Solution[J].Surface Technology,2016,45(1):124-130,160
电化学法研究芭蕉叶提取物在盐酸中对碳钢的缓蚀作用
Electrochemical Investigation of Extracts of Musa Basjoo Leaves as Corrosion Inhibitor for Carbon Steel in Hydrochloric Acid Solution
投稿时间:2015-09-20  修订日期:2016-01-20
DOI:10.16490/j.cnki.issn.1001-3660.2016.01.020
中文关键词:  碳钢  盐酸  芭蕉叶  缓蚀  极化曲线  电化学阻抗图谱
英文关键词:carbon steel  hydrochloric acid  Musa basjoo leaves  corrosion inhibition  polarization curves  electrochemical impedance spectroscopy
基金项目:国家自然科学基金(51361001);楚雄师范学院学术骨干培养项目(12YJGG02)
作者单位
陈文 楚雄师范学院 化学与生命科学学院, 云南 楚雄 675000 
陶永元 楚雄师范学院 化学与生命科学学院, 云南 楚雄 675000 
管春平 楚雄师范学院 化学与生命科学学院, 云南 楚雄 675000 
胡小安 楚雄师范学院 应用化学技术研究所, 云南 楚雄 675000 
AuthorInstitution
CHEN Wen School of Chemistry and Life Sciences, Chuxiong Normal University, Chuxiong 675000, China 
TAO Yong-yuan School of Chemistry and Life Sciences, Chuxiong Normal University, Chuxiong 675000, China 
GUAN Chun-ping School of Chemistry and Life Sciences, Chuxiong Normal University, Chuxiong 675000, China 
HU Xiao-an Applied Chemistry and Technology Laboratory, Chuxiong Normal University, Chuxiong 675000, China 
摘要点击次数:
全文下载次数:
中文摘要:
      目的 研究芭蕉叶提取物(MBLE)在酸性环境中对碳钢腐蚀的抑制行为。 方法 通过热水浸提法获取 MBLE,采用电化学方法研究在不同实验温度和不同浓度下 MBLE 在 1 mol/ L 盐酸溶液中对碳钢的缓蚀行为,并用扫描电镜(SEM)研究金属表面腐蚀形貌。 结果 极化曲线研究表明,MBLE 对碳钢在 1mol/ L 盐酸中的腐蚀有明显抑制作用,属阴极抑制为主的混合型缓蚀剂;其缓蚀性能随质量浓度增大而增强,25 ℃时 160 mg/ L 的 MBLE 缓蚀效率达到 94. 7 % 。 电化学阻抗图谱研究表明,随着 MBLE 质量浓度的增大,碳钢表面腐蚀反应的电荷转℃电阻逐渐增大,腐蚀反应抑制程度增强。 变温试验研究表明,MBLE 在实验温度范围内具有较好的稳定性。 当 MBLE 质量浓度为 160 mg/ L 时,温度从 25 ℃增加到 40℃ ,两种电化学方法所得缓蚀效率的变化幅度均在 3% 以内。 MBLE 缓蚀剂分子在碳钢表面的吸附服从Dhar-Flory-Huggins 等温吸附式,并且属于物理和化学混合吸附。 SEM 研究表明,盐酸介质中 MBLE 可有效地抑制碳钢的腐蚀。 结论 对碳钢在盐酸介质中的腐蚀,MBLE 是有效的绿色缓蚀剂。
英文摘要:
      Objective To investigate the inhibitive action of extracts of Musa basjoo leaves (MBLE) on the corrosion of carbon steel in acidic medium. Methods MBLE was achieved by hot water extraction method, and its inhibition effect on the carbon steel corrosion in 1 mol/ L HCl solution at different temperatures and extract concentrations was investigated by electrochemical methods. The surface morphology of the carbon steel was examined by scanning electron microscopy (SEM) both in the absence of an inhibitor and in the presence of a MBLE-containing corrosive medium. Results The obtained results of polarization curves indicated that MBLE acted as a mixed-type inhibitor with a preferential effect on cathodic reaction for steel corrosion in 1 mol / L HCl solution. The inhibition efficiency was found to increase with increasing MBLE concentration and reached up to maximum 94. 7 % at the MBLE concentration of 160 mg / L at 25 ℃ . The analysis of electrochemical impedance spectroscopy implied that the charge transfer resistance of surface corrosion reaction increased with increasing MBLE concentration, which could lead to more effective suppression of the corrosion reaction. Changing-temperature measurements indicated that the inhibition of MBLE had a preferable thermal stability within the range of experiment temperature. When the temperature increased from 25 ℃ to 40 ℃ , the variations of inhibition efficiency obtained by the two electrochemical methods at MBLE concentration of 160 mg / L were less than 3% . The adsorption of MBLE molecules on the steel surface obeyed the Dhar-Flory-Huggins adsorption isotherm and was a spontaneous adsorption process including both physisorption and chemisorption. The SEM observations showed that MBLE could effectively inhibit steel corrosion. Conclusion MBLE is an effective and environmentally friendly inhibitor for carbon steel in HCl medium.
查看全文  查看/发表评论  下载PDF阅读器
关闭

关于我们 | 联系我们 | 投诉建议 | 隐私保护 | 用户协议

您是第19504495位访问者    渝ICP备15012534号-3

版权所有:《表面技术》编辑部 2014 surface-techj.com, All Rights Reserved

邮编:400039 电话:023-68792193传真:023-68792396 Email: bmjs@surface-techj.com

渝公网安备 50010702501715号