邓红华,夏琴香,程秀全,任艳萍.喷丸对预腐蚀后铝合金疲劳性能的影响[J].表面技术,2016,45(1):118-123.
DENG Hong-hua,XIA Qin-xiang,CHENG Xiu-quan,REN Yan-ping.Effects on Anti-corrosion Fatigue Property of Aluminum Alloy after Shot Peening[J].Surface Technology,2016,45(1):118-123
喷丸对预腐蚀后铝合金疲劳性能的影响
Effects on Anti-corrosion Fatigue Property of Aluminum Alloy after Shot Peening
投稿时间:2015-09-17  修订日期:2016-01-20
DOI:10.16490/j.cnki.issn.1001-3660.2016.01.019
中文关键词:  喷丸  预腐蚀  铝合金  疲劳性能  航空构件  断裂位置
英文关键词:shot peening  pre-corrosion  aluminum alloy  fatigue property  aircraft component  fracture location
基金项目:国家自然科学基金资助项目(51575117);国家自然科学基金(民航联合基金)资助项目(61179051)
作者单位
邓红华 广州民航职业技术学院 飞机维修工程学院, 广州 510470 
夏琴香 华南理工大学 机械与汽车工程学院, 广州 510640 
程秀全 广州民航职业技术学院 飞机维修工程学院, 广州 510470 
任艳萍 广州民航职业技术学院 飞机维修工程学院, 广州 510470 
AuthorInstitution
DENG Hong-hua School of Aircraft Maintenance Engineering, Guangzhou Civil Aviation College, Guangzhou 510470, China 
XIA Qin-xiang School of Mechanical and Automotive Engineering, South China University of Technology, Guangzhou 510640, China 
CHENG Xiu-quan School of Aircraft Maintenance Engineering, Guangzhou Civil Aviation College, Guangzhou 510470, China 
REN Yan-ping School of Aircraft Maintenance Engineering, Guangzhou Civil Aviation College, Guangzhou 510470, China 
摘要点击次数:
全文下载次数:
中文摘要:
      目的 分析喷丸对铝合金腐蚀损伤构件疲劳性能的影响,为飞机构件的维修提供有效指导。 方法 以未喷丸、三面喷丸、三面喷丸腐蚀后再三面喷丸 3 类不同表面状态的 7075 铝合金试样为研究对象,改变 NaCl 溶液质量分数、时间、温度,获得两种程度不同的腐蚀损伤,通过疲劳寿命、断裂位置、断口形貌,分析表面喷丸状态对铝合金疲劳性能的影响。 结果 腐蚀损伤较轻时,喷丸试样的疲劳寿命为未喷丸试样的 7. 84 倍,喷丸试样腐蚀后若再喷丸处理,疲劳寿命是不再喷丸试样的 1. 62 倍。 未喷丸试样的断裂位置位于截面突变颈部区域,另两类喷丸试样的断裂位置则在夹持段前端。 未喷丸试样的裂纹在断口表面的边缘位置形成,喷丸试样的中心区域形成光滑平整的稳态扩展区。 腐蚀损伤严重时,喷丸处理仍然会提高铝合金的疲劳寿命,但 3 类不同表面状态试样的疲劳寿命差距会缩小;从试样断裂位置、断口形貌看,3 类试样的差异也会弱化。 结论 铝合金腐蚀损伤件若腐蚀前进行表面先喷丸处理,疲劳性能会有明显提升;若腐蚀后再喷丸处理,疲劳性能还会进一步提升;喷丸处理还会削弱铝合金外形截面突变处的应力集中,抑制疲劳裂纹在构件表面的萌生及延伸。
英文摘要:
      Objective To analyze the influence of shot peening on fatigue performance of aluminum alloy components with corrosion damage so as to guide the repair of aircraft components. Methods The 7075 aluminum alloy samples with three types of different surface states, which were treated with un-shot peening, shot peening on three surfaces and shot peening for twice on three surfaces, were selected as the research subjects. The corrosion damage of two different degrees was obtained by changing the corrosion parameters such as NaCl concentration, temperature and time, and the fatigue property of aluminum alloy on shot peening surface state was analyzed according to fatigue life, fracture location and fracture morphology of aluminum alloy. Results At a mild corrosion damage, the fatigue life of shot peening on three surface was 7. 84 times longer than that of un-shot peening, and the fatigue life would be further improved by 1. 62 times if the eroded sample after shot peening was peened again; the fracture position of unshot peening sample was located in the abruptly changed area of cross section, and the fracture position of the other two types of shot peened samples was in the front of clip. According to observation of the fracture morphology, fatigue crack of un-shot peening samples showed that on the edge of the fracture surface, the central regions of shot peened sample formed a smooth and straight stable-extended area. At a serious corrosion damage, shot peening processing still could improve the fatigue life of aluminum alloy, but the fatigue life gap would be reduced on three kinds of different surface samples. According to observation of the fracture position and the fracture morphology, the gap was also narrowed between three kinds of samples. Conclusion The fatigue performance would be improved obviously, if the aluminum alloy corrosion damage components were shot peened before pre-corrosion treatments; and the fatigue performance of materials would be further improved, if the eroded sample after shot peening were peened again; besides, the stress concentration would be weaken on the abruptly changed area of cross-section, and production and growth of fatigue crack would be restrained on the component surface when the aluminum alloy component was shot peened.
查看全文  查看/发表评论  下载PDF阅读器
关闭

关于我们 | 联系我们 | 投诉建议 | 隐私保护 | 用户协议

您是第19513744位访问者    渝ICP备15012534号-3

版权所有:《表面技术》编辑部 2014 surface-techj.com, All Rights Reserved

邮编:400039 电话:023-68792193传真:023-68792396 Email: bmjs@surface-techj.com

渝公网安备 50010702501715号