张德强,张吉庆,郭忠娟.45# 钢表面激光熔覆自熔性镍基碳化钨粉末[J].表面技术,2015,44(11):66-70.
ZHANG De-qiang,ZHANG Ji-qing,GUO Zhong-juan.Laser Cladding of Self-fluxing Ni-based WC Powder on 45# Steel Surface[J].Surface Technology,2015,44(11):66-70
45# 钢表面激光熔覆自熔性镍基碳化钨粉末
Laser Cladding of Self-fluxing Ni-based WC Powder on 45# Steel Surface
投稿时间:2015-06-10  修订日期:2015-11-20
DOI:10.16490/j.cnki.issn.1001-3660.2015.11.011
中文关键词:  激光熔覆  自熔性镍基碳化钨  工艺参数  宏观表面  表面硬度  金相组织  显微硬度
英文关键词:laser cladding  self-fluxing nickel based WC  process parameters  macroscopic surface  surface hardness  microstructure  microhardness
基金项目:国家科技支撑计划项目(2012BAF12B08-5)
作者单位
张德强 辽宁工业大学 机械工程与自动化学院, 辽宁 锦州 121001 
张吉庆 辽宁工业大学 机械工程与自动化学院, 辽宁 锦州 121001 
郭忠娟 日照港油品码头有限公司, 山东 日照 276800 
AuthorInstitution
ZHANG De-qiang Faculty of Mechanical Engineering and Automation, Liaoning University of Technology, Jinzhou 121001, China 
ZHANG Ji-qing Faculty of Mechanical Engineering and Automation, Liaoning University of Technology, Jinzhou 121001, China 
GUO Zhong-juan Rizhao Port Oil Terminal Co. , Ltd, Rizhao 276800, China 
摘要点击次数:
全文下载次数:
中文摘要:
      目的 提高 45#钢的表面性能。 方法 利用 IPG 光纤激光加工系统,采用不同的工艺参数在 45#钢表面激光熔覆自熔性镍基碳化钨粉末,对熔覆层的宏观表面(平整度、表面硬度、裂纹情况)及金相组织、显微硬度分布进行对比分析。 结果 在激光功率为 1200 W、扫描速度为 2 mm/ s、送粉电压为 7 V 时,获得的熔覆层宏观表面相对平整光滑,平均洛氏硬度约是基体的 2. 5 倍。 由微观组织分析得知,熔覆层及界面处无裂纹、气孔等缺陷,熔覆层中上部组织晶粒细小,沿熔覆层与基体交界处向外,晶粒呈现柱状晶及等轴晶,组织性能良好,基体与熔覆层间冶金结合比较牢固。 熔覆层显微硬度分布比较均匀,并且与基体相比提高了约 1. 5 倍。 结论 45#钢表面机械性能得到提升,在其表面激光熔覆自熔性镍基碳化钨粉末具有可行性和研究价值。
英文摘要:
      Objective To improve the surface properties of 45# steel. Methods Using IPG fiber laser YLR-3000 Laser Processing System, laser cladding of self-fluxing Ni-based WC Powders was conducted on the surface of 45# steel using different process parameters. Comparative analysis was conducted on the macroscopic surface (Flatness, surface hardness, cracks), metallurgical structure and distribution of microhardness of the cladding layer. Results When the laser power was 1200 W, scanning speed was 2 mm/ s, and powder feeding voltage was 7 V, the cladding layer had relatively smooth macro surface, and the average Rockwell hardness of the cladding layer was about 2. 5 times that of the matrix. The microstructure analysis showed that there were no defects such as cracks and holes in the cladding layer and the interface, the middle and upper part of the cladding layer had fine grains, the grains were dendritic and equiaxed along the interface of the cladding layer and the substrate, the structural performance was good, and the metallurgical bonding between the cladding layer and the substrate was relatively strong. The microhardness distribution of the cladding layer was relatively even, and increased by about 1. 5 times as compared to the substrate. Conclusion The mechanical properties of 45# steel surface were improved. Laser cladding of self-fluxing nickel-based tungsten carbide powder on its surface has therefore feasibility and research value.
查看全文  查看/发表评论  下载PDF阅读器
关闭

关于我们 | 联系我们 | 投诉建议 | 隐私保护 | 用户协议

您是第19507732位访问者    渝ICP备15012534号-3

版权所有:《表面技术》编辑部 2014 surface-techj.com, All Rights Reserved

邮编:400039 电话:023-68792193传真:023-68792396 Email: bmjs@surface-techj.com

渝公网安备 50010702501715号