张雅雅,崔建国.基于微波放电法的 PDMS 材料表面改性[J].表面技术,2015,44(9):78-83.
ZHANG Ya-ya,CUI Jian-guo.PDMS Surface Modification Based on Microwave Discharge[J].Surface Technology,2015,44(9):78-83
基于微波放电法的 PDMS 材料表面改性
PDMS Surface Modification Based on Microwave Discharge
投稿时间:2015-06-02  修订日期:2015-09-20
DOI:10.16490/j.cnki.issn.1001-3660.2015.09.013
中文关键词:  微波放电  低温等离子体  PDMS  接触角  键合强度
英文关键词:microwave discharge  low-temperature plasma  PDMS  contact angle  bonding strength
基金项目:科技部科技支撑计划(2015BAI01B14);重庆理工大学实验技术基金项目( Sk201403);重庆理工大学研究生教育教学改革项目(yjg2013205)
作者单位
张雅雅 重庆理工大学 药学与生物工程学院, 重庆 400054 
崔建国 重庆理工大学 药学与生物工程学院, 重庆 400054 
AuthorInstitution
ZHANG Ya-ya School of Pharmacy & Bioengineering, Chongqing University of Technology, Chongqing 400054, China 
CUI Jian-guo School of Pharmacy & Bioengineering, Chongqing University of Technology, Chongqing 400054, China 
摘要点击次数:
全文下载次数:
中文摘要:
      目的 研究微波放电法对聚二甲基硅氧烷(PDMS)材料表面的改性效果。 方法 利用家用微波炉的微波作用以及自制的真空罩电极装置,产生低温等离子体放电,对 PDMS 材料表面进行激活处理。对处理后的 PDMS 材料表面接触角的恢复情况以及 PDMS 间的键合强度进行实验测试。 结果 微波放电处理后的 PDMS 材料表面初始呈现出很强的亲水性,当微波功率为 140 W,工作 5 s 时,PDMS 表面接触角可达到 10°左右;通过?旆⑾炙孀欧胖檬奔涞脑黾?PDMS 材料表面接触角逐渐增大且在 10 天后恢复到原始疏水角状态;同时,经过改性的 PDMS 样品之间可实现较好的键合封装,其最优键合条件为 80℃ +1. 5 h 压合,其键合强度可达到 12. 4 N。 结论 使用微波放电法处理 PDMS 材料表面,可成功地对材料进行亲水改性处理,并实现 PDMS 间的很好键合。 与传统等离子体处理键合方法相比,该方法简单、经济且高效。
英文摘要:
      Objective To study the modification effect of microwave discharge of PDMS materials. Methods PDMS was activated by the low-temperature plasma discharge produced by household microwave oven and the self-made vacuum hood electrode device. The recovery of the surface contact angle and the bonding strength of the modified PDMS were experimentally tested. Results After microwave discharge treatment, the PDMS surface showed strong hydrophilicity at the beginning, when the microwave power was 140 W and the working time was 5 s, the PDMS surface contact angle could reach 10°. Through observation, it was found that with the increase of storage time, the PDMS surface contact angle increased gradually and after 10 d it returned to the original hydrophobic angle state. At the same time, good bonding was achieved between the modified PDMS samples, and the optimal bonding condition was 80 ℃ for 1. 5 h, under this condition the bonding strength could reach 12. 4 N. Conclusion After treatment with microwave discharge method, the PDMS materials surface could be successfully modified to be hydrophilic, and good bonding could be achieved between PDMS. Compared with the traditional plasma processing bonding method, this method is simple, economic and efficient.
查看全文  查看/发表评论  下载PDF阅读器
关闭

关于我们 | 联系我们 | 投诉建议 | 隐私保护 | 用户协议

您是第13543783位访问者    渝ICP备15012534号-3

版权所有:《表面技术》编辑部 2014 surface-techj.com, All Rights Reserved

邮编:400039 电话:023-68792193传真:023-68792396 Email: wjqkbm@163.com

渝公网安备 50010702501715号